Steel sheet having high young's modulus, hot-dip galvanized steel sheet using the same, alloyed hot-dip galvanized steel sheet, steel pipe having high young's modulus, and methods for manufacturing the same

Abstract

In an embodiment of a steel sheet having high Young's modulus, the steel can include in terms of mass %, e.g., C: 0.0005 to 0.30%, Si: 2.3% or less, Mn: 2.7 to 5.0%, P: 0.15% or less, 0.015% or less, Mo: 0.15 to 1.5%, B: 0.0006 to 0.01%, and Al: 0.15% or less, with the remainder being Fe and unavoidable impurities. One or both of {110}<223> pole density and {110}<111> pole density in the ⅛ sheet thickness layer can be 10 or more, and a Young's modulus in a rolling direction can be more than 230 GPa. Other embodiments can include, e.g., Mn: 0.1 to 5.0%, N: 0.01% or less, and one or more of Mo: 0.005 to 1.5%, Nb: 0.005 to 0.20%, Ti: at least 48/14×N (mass %) and 0.2% or less, and B: 0.0001 to 0.01%, at a total content of 0.015 to 1.91 mass %.