Soft and flexible polyolefin compositions
AssigneeBasell Poliolefine Italia S.r.l.
InventorsGiampaolo Pellegatti, Paolo Goberti
Life of this patent
Estimating the term…
Abstract
A polyolefin composition having unusually low values of flexural modulus and shore hardness and comprising, in percent by weight: A) 15-40% of a copolymer of propylene with hexene-1 containing from 2.5 to 10% of hexene-1 and having Melt Flow Rate (MFR, measured according to ISO 1133, 230° C./2.16 Kg) from 0.5 to 100 g/10 min.; and B) 60-85% of an ethylene copolymer containing ethylene in a quantity equal to or lower than 40%, and having solubility in xylene at room temperature greater than 70%.
Claims7
A polyolefin composition consisting of the following components, all percent amounts being by weight:
- A) 15-40% of a copolymer of propylene with hexene-1 containing from 2.5 to 10% of hexene-1 and having a melt flow rate, measured according to ISO 1133 at 230° C./2.16 kg, from 0.5 to 100 g/10 min., and having a melting point from 125 to 150° C.;
- and
- B) 60-85% of a copolymer of ethylene with propylene or a CH2═CHR α-olefin, where R is a C2-C8 alkyl radical, and optionally minor quantities of a diene present in an amount from 1 to 10% by weight, or a copolymer of ethylene with propylene and said α-olefin, and optionally a diene, present in an amount from 1 to 10% by weight, said copolymers containing ethylene in a quantity equal to or lower than 40%, and having a solubility in xylene at room temperature greater than 70%,
- wherein the polyolefin composition has a melt flow rate from 0.6 to 15 g/10 min, measured according to ISO 1133 at 230° C./2.16 kg.
A polyolefin composition consisting of the following components, all percent amounts being by weight:
- A) 26-35% of a copolymer of propylene with hexane-1 containing from 2.5 to 10% of hexane-1 and having a melt flow rate, measured according to ISO 1133 at 230° C./2.16 kg, from 0.5 to 100 g/10 min., and having a melting point from 125 to 150° C.;
- and
- B) 65-74% of a copolymer of ethylene with propylene or a CH2═CHR α-olefin, where R is a C2-C8 alkyl radical, and optionally a diene present in an amount from 1 to 10% by weight, or a copolymer of ethylene with propylene and said α-olefin, and optionally a diene, present in an amount from 1 to 10% by weight, said copolymers containing ethylene in a quantity equal to or lower than 40%, and having a solubility in xylene at room temperature greater than 70%, the polyolefin composition having a melt flow rate of from 0.6 to 15 g/10 min according to ISO 1133 measured at 230° C./2.16 kg.
Dependencies are inferred from the claim text.