# US 8,784,961 B2 · Fluoropolymer blends with inorganic layered compounds > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 8,784,961 B2 - Document ID: US8784961B2 - Status: Granted - Kind: B2 - Application number: 12/482,633 - Filed: 2009-06-11 - Published: 2009-12-03 - Granted: 2014-07-22 - Earliest claimed: 2006-10-02 - Assignees: DuPont-Mitsui Fluorochemicals Co., Ltd. - Applicants: Pham Hoai Nam; Jeong Chang Lee; Kenji Oki; Hajime Sato - Inventors: Pham Hoai Nam; Jeong Chang Lee; Kenji Oki; Hajime Sato - Web page: https://patentgrep.com/patent/US8784961B2 ## CPC - C08F 214/262: {with fluorinated vinyl ethers} - C08K 3/34: Silicon-containing compounds - C08L 27/12: containing fluorine atoms - B29K 2027/12: containing fluorine - Y10T 428/139: Open-ended, self-supporting conduit, cylinder, or tube-type article - Y10T 428/265: 1 mil or less - Y10T 428/269: including synthetic resin or polymer layer or component - Y10T 428/2982: Particulate matter [e.g., sphere, flake, etc.] - C08F: MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS - C08K: Use of inorganic or non-macromolecular organic substances as compounding ingredients (paints, inks, varnishes, dyes, polishes, adhesives C09) - C08L: COMPOSITIONS OF MACROMOLECULAR COMPOUNDS (compositions based on polymerisable monomers C08F, C08G; artificial filaments or fibres D01F; textile treating compositions D06) - B29K: INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR {MOULDS, } REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS - Y10T: TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION ## Abstract Perfluoropolymer composites are provided which are obtained by dispersing layered-silicates having properties of swelling or cleaving in dispersion media in perfluoropolymers and having the ratio of the viscosity, V0.1, at 0.1 rad/sec by a parallel plate mode of a dynamic rheometer to the viscosity, V1, measured at 1 rad/sec is 1.5 or greater, viscosity being measured at 340° C. A method for making the perfluoropolymer composites is provided, and molded articles therefrom. And additionally, perfluoropolymer composites, where layered-silicates having properties of swelling or cleaving in dispersion media are dispersed in perfluoropolymers, with the storage elasticity of 2 times or higher than that of fluoropolymers, at temperatures greater than the glass transition temperature of perfluoropolymers. ## Claims ### Claim 1 Perfluoropolymer composite obtained by dispersing layered-silicate having properties of swelling or cleaving in water to form an aqueous dispersion of said layered-silicate, adding said aqueous dispersion to an aqueous dispersion of perfluoropolymer having a melt flow rate of 0.5 to 100 g/10 min and agglomerating the resultant mixture of dispersions by changing the ionic strength or pH of said resultant mixture by adding 0.001 to 5 weight percent of electrolyte thereto based on the combined weight of said aqueous dispersion of layered-silicate and said aqueous dispersion of perfluoropolymer, and applying shear to obtain as a result thereof said perfluoropolymer composite comprising a dispersion of particles of said layered-silicate homogeneously dispersed at the nano-level in said perfluoropolymer, wherein the layer thickness of said layered-silicate in said perfluoropolymer composite is less than about 25 nm, and wherein the ratio of the storage elasticity (G′s) of the perfluoropolymer composite to the storage elasticity (G′F) of the perfluoropolymer, G′s/G′F, is 3 or greater at temperatures greater than the glass transition temperature of said perfluoropolymer, said perfluoropolymer being a copolymer of tetrafluoroethylene and perfluoro(alkyl vinyl ether), wherein said alkyl contains from 1 to 5 carbon atoms. ### Claim 2 (depends on 1) The composite of claim 1, wherein said layered-silicate having properties of swelling or cleaving in the said dispersion media is at least one layered-silicate selected from the group consisting of smectite-group clay minerals and swelling mica-group clay minerals. ### Claim 3 (depends on 1) The composite of claim 1, wherein said the content of layered-silicate in said perfluoropolymer composite is 0.5-15% by weight with respect to the perfluoropolymer composite. ### Claim 4 (depends on 1) A method of producing the perfluoropolymer composite of claim 1 by mixing an aqueous dispersion of perfluoropolymer having a melt flow rate of 0.5 to 100 g/10 min with an aqueous dispersion containing layered-silicate having properties of swelling or cleaving in dispersion media under stirring to obtain mixed aqueous dispersion, agglomerating said mixed aqueous dispersion of perfluoropolymer and layered-silicate by changing the ionic strength or the pH by adding electrolyte thereto and applying shear, separating the aqueous components from the agglomerates, and drying to obtain as a result thereof the dispersion of said layered-silicate in said perfluoropolymer, wherein the ratio of the storage elasticity (G′s) of the perfluoropolymer composite to the storage elasticity (G′F) of the perfluoropolymer, G′s/GF′, is 3 or greater at temperatures greater than the glass transition temperature of said perfluoropolymer, said perfluoropolymer being a copolymer of tetrafluoroethylene and perfluoro(alkyl vinyl ether), wherein said alkyl contains from 1 to 5 carbon atoms. ### Claim 5 (depends on 1) Pellets obtained by melt-extruding the perfluoropolymer composite of claim 1. ### Claim 6 Insulated conductor or jacket for insulated conductor made by extrusion of perfluoropolymer composite obtained by dispersing layered-silicate having properties of swelling or cleaving in water to form an aqueous dispersion of said layered-silicate, adding said aqueous dispersion to an aqueous dispersion of perfluoropolymer having a melt flow rate of 0.5 to 100 g/10 min and agglomerating the resultant mixture of dispersions by changing the ionic strength or pH of said resultant mixture by adding 0.001 to 5 weight percent of electrolyte thereto based on the combined weight of said aqueous dispersion of layered-silicate and said aqueous dispersion of perfluoropolymer, and applying shear to obtain as a result thereof said perfluoropolymer composite comprising a dispersion of particles of said layered-silicate homogeneously dispersed at the nano-level in said perfluoropolymer, wherein the layer thickness of said layered-silicate in said perfluoropolymer composite is less than about 25 nm, and wherein the ratio of the storage elasticity (G′s) of the perfluoropolymer composite to the storage elasticity (G′F) of the perfluoropolymer, G′s/GF′, is 3 or greater at temperatures of 60° C. or greater than the glass transition temperature of said perfluoropolymer, said perfluoropolymer being a copolymer of tetrafluoroethylene and perfluoro(alkyl vinyl ether), wherein said alkyl contains from 1 to 5 carbon atoms. ### Claim 7 (depends on 6) The insulated conductor or jacket for insulated conductor of claim 6, wherein said perfluoropolymer composite has the ratio (V0.1/V1) of the viscosity (V0.1) measured at 340° C. and 0.1 rad/sec by parallel plate mode of a dynamic rheometer to the viscosity (V1) measured at 340° C. and 1 rad/sec is 1.5 or greater. ### Claim 8 (depends on 1) Tube, sheet, or film made from the perfluoropolymer composite of claim 1. ### Claim 9 (depends on 1) Blow-molded articles made from the perfluoropolymer composite of claim 1. ### Claim 10 (depends on 1) Injection molded articles made from the perfluoropolymer composite of claim 1. ### Claim 11 Perfluoropolymer composite obtained by dispersing layered-silicate having properties of swelling or cleaving in water to form an aqueous dispersion of said layered-silicate, adding said aqueous dispersion to an aqueous dispersion of perfluoropolymer having a melt flow rate of 0.5 to 100 g/10 min, and agglomerating the resultant mixture of dispersions by adding 0.001 to 5 weight percent of electrolyte thereto based on the combined weight of said aqueous dispersion of layered-silicate and said aqueous dispersion of perfluoropolymer, and applying shear to obtain as a result thereof said perfluoropolymer composite comprising a dispersion of said layered-silicate homogeneously dispersed at the nano-level in said perfluoropolymer wherein the layer thickness of said layered-silicate in said perfluoropolymer composite is less than about 25 nm, and wherein the X-ray diffraction peak for the layered silicate, visible in said aqueous dispersion of said layered silicate, is not visible in said dispersion of layered silicate in said perfluoropolymer, wherein the ratio of the storage elasticity (G′s) of the perfluoropolymer composite to the storage elasticity (G′F) of the perfluoropolymer, G′s/GF′, is 3 or greater at temperatures greater than the glass transition temperature of said perfluoropolymer, said perfluoropolymer being a copolymer of tetrafluoroethylene and perfluoro(alkyl vinyl ether), wherein said alkyl contains from 1 to 5 carbon atoms. ### Claim 12 (depends on 11) The perfluoropolymer composite of claim 11, wherein said temperature greater than the glass transition temperature of said perfluoropolymer is at least 60° C. higher than said glass transition temperature. ### Claim 13 (depends on 1) The perfluoropolymer composite of claim 1, wherein said temperature greater than the glass transition temperature of said perfluoropolymer is at least 60° C. higher than said glass transition temperature. ### Claim 14 (depends on 4) The method of claim 4, wherein said temperature greater than the glass transition temperature of said perfluoropolymer is at least 60° C. higher than said glass transition temperature.