# US 8,784,725 B2 · Wide casting belt, method for manufacturing a wide film, and wide film

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 8,784,725 B2
- Document ID: US8784725B2
- Status: Granted
- Kind: B2
- Application number: 13/375,985
- Filed: 2009-06-04
- Published: 2012-05-24
- Granted: 2014-07-22
- Earliest claimed: 2009-06-04
- Assignees: SK Innovation Co., Ltd.
- Applicants: Hyukjun Kim; Kwangjin Chung; Cholho Lee; Yooseock Hwang; Juntae Choi; Kinam Chung
- Inventors: Hyukjun Kim; Kwangjin Chung; Cholho Lee; Yooseock Hwang; Juntae Choi; Kinam Chung
- Web page: https://patentgrep.com/patent/US8784725B2

## CPC

- B29D 7/01: Films or sheets
- B29C 41/28: by depositing flowable material on an endless belt
- B29C 41/34: Component parts, details or accessories; Auxiliary operations
- B29C 41/38: Moulds, cores or other substrates
- C08J 5/18: Manufacture of films or sheets
- B29K 2001/12: {Cellulose acetate}
- C08J 2301/12: Cellulose acetate
- Y10T 428/24802: Discontinuous or differential coating, impregnation or bond [e.g., artwork, printing, retouched photograph, etc.]
- B29D: PRODUCING PARTICULAR ARTICLES FROM PLASTICS OR FROM SUBSTANCES IN A PLASTIC STATE (making granules B29B9/00; making preforms B29B11/00)
- B29C: SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING (making preforms B29B11/00; making laminated products by combining previously unconnected layers which become one product whose layers will remain together B32B37/00 - B32B41/00)
- C08J: WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H (working, e.g. shaping, of plastics B29)
- B29K: INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR {MOULDS, } REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
- Y10T: TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION

## Abstract

The present invention relates to a wide casting belt, and more particularly, to a wide casting belt used for manufacturing a film in a gel state by casting dope used during the manufacture of a polarizing plate for a liquid crystal display, and an optical compensation film, etc. The present invention also relates to a method for manufacturing a wide film using the wide casting belt, and to a wide film manufactured with said wide casting belt.

## Claims

### Claim 1

A method for manufacturing a wide film using a wide casting belt, comprising:
casting a dope containing a cellulose triacetate solution on the wide casting belt to form a gel type film, the wide casting belt being formed of a central belt having a central belt joint, a left belt having a left belt joint and a right belt having a right belt joint, wherein the central belt joint, the left belt joint and the right belt joint are formed, respectively, at an angle of 0° to 25° to a transverse face of the wide casting belt;
stretching the gel type film stripped off from the wide casting belt, using a tenter;
a first trimming process of removing a mark part caused by gripping left and right parts of the stretched film using the tenter during stretching;
drying the film obtained from the first trimming process, using a dryer;
a second trimming process of removing some parts at left and right sides of the film to smoothly transport the film and maintain overall characteristics of the film, after the drying process;
marking anti-slipping mark on the left and right sides of the trimmed parts to prevent the film from being damaged while winding the film, enable the film to be wound in large quantities while winding, and prevent generation of a black belt after film winding, after the second trimming process; and
winding the marked film.

### Claim 2 (depends on 1)

The method of claim 1, wherein the dope has a solid content comprising cellulose triacetate and a plasticizer, wherein the dope includes a solvent including a mixed solution of methylene chloride and methanol; and wherein a mixing ratio of the methylene chloride and the methanol ranges from 80:20 to 95:5, while the plasticizer is contained in an amount of 5 to 20 wt. %, relative to 100 wt. % of the cellulose triacetate.

### Claim 3 (depends on 2)

The method of claim 2, wherein, if the gel type film stripped off from the wide casting belt has a width of CW and the film obtained from the stretching process has a width of TW, the film has CW≧1300 mm; and CW×0.9≦TW≦CW×1.3.