# US 8,771,455 B2 · Process for production of composite fine particles with heterogeneous surfaces > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 8,771,455 B2 - Document ID: US8771455B2 - Status: Granted - Kind: B2 - Application number: 13/575,649 - Filed: 2010-12-13 - Published: 2013-01-10 - Granted: 2014-07-08 - Earliest claimed: 2010-01-27 - Assignees: Niigata University; Sekisui Chemical Co., Ltd. - Applicants: Masato Tanaka - Inventors: Masato Tanaka - Web page: https://patentgrep.com/patent/US8771455B2 ## CPC - C08J 3/12: Powdering or granulating - B29B 9/04: in the form of plates or sheets - C08F 2/02: Polymerisation in bulk - C08F 2/44: Polymerisation in the presence of compounding ingredients, e.g. plasticisers, dyestuffs, fillers - C08F 292/00: Macromolecular compounds obtained by polymerising monomers on to inorganic materials - B29B 2009/125: {Micropellets, microgranules, microparticles} - C08J 2367/02: Polyesters derived from dicarboxylic acids and dihydroxy compounds; (C08J2367/06 takes precedence) - Y10T 156/1052: with cutting, punching, tearing or severing - C08J: WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H (working, e.g. shaping, of plastics B29) - B29B: PREPARATION OR PRETREATMENT OF THE MATERIAL TO BE SHAPED; MAKING GRANULES OR PREFORMS; RECOVERY OF PLASTICS OR OTHER CONSTITUENTS OF WASTE MATERIAL CONTAINING PLASTICS - C08F: MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS - Y10T: TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION ## Abstract Provided is a process for production of composite fine particles with heterogeneous surfaces. The process ensures a high productivity and enables a voluntary control of particle diameters. Further, the process imposes no restrictions on heterogeneous substances added for functional expression, and allows a heterogeneous substance to be encapsulated in central portions of composite fine particle spheres. A composite film obtained by laminating two or more kinds of films is cut into minute pieces, followed by melting the same to obtain spherical minute pieces. Particularly, liquid films are separately formed with two or more kinds of liquids containing polymerizable monomers. Further, two or more kinds of films can thereby be obtained through polymerization. The two or more kinds of films thus obtained are then laminated to further allow polymerization to take place, thus obtaining the composite film. ## Claims ### Claim 1 A process for production of composite fine particles with heterogeneous surfaces, comprising: forming two or more kinds of liquids, each containing a polymerizable monomer, into two or more kinds of liquid films respectively; subjecting said liquid films to polymerization to form two or more kinds of films; laminating said two or more kinds of films to form a composite film; subjecting the composite film to further polymerization; a step of cutting the composite film into minute pieces; and a step of melting said minute pieces. ### Claim 2 (depends on 1) The process for production of composite fine particles with heterogeneous surfaces according to claim 1, wherein said composite film is cut into minute pieces of substantially cubical shapes, followed by melting said minute pieces into spherical minute pieces. ### Claim 3 (depends on 1) The process for production of composite fine particles with heterogeneous surfaces according to claim 1, wherein said composite film is cut into minute pieces in the form of substantially quadrangular prisms, followed by melting said minute pieces into cylindrical minute pieces. ### Claim 4 (depends on 1) The process for production of composite fine particles with heterogeneous surfaces according to claim 1, wherein said composite film is cut by a laser cutter. ### Claim 5 (depends on 1) The process for production of composite fine particles with heterogeneous surfaces according to claim 1, wherein said composite film is prepared by laminating: one film obtained by forming a liquid containing a polymerizable monomer and an electrically conductive material into a liquid film and then subjecting the same to polymerization; and another film obtained by forming a liquid containing a polymerizable monomer and an electrically insulative material into a liquid film and then subjecting the same to polymerization, followed by subjecting the films thus laminated to further polymerization. ### Claim 6 (depends on 1) The process for production of composite fine particles with heterogeneous surfaces according to claim 1, wherein said composite film is prepared by laminating: one film obtained by forming a liquid containing a polymerizable monomer and an anionic polymerization initiator into a liquid film and then subjecting the same to polymerization; and another film obtained by forming a liquid containing a polymerizable monomer and a cationic polymerization initiator into a liquid film and then subjecting the same to polymerization, followed by subjecting the films thus laminated to further polymerization. ### Claim 7 (depends on 1) The process for production of composite fine particles with heterogeneous surfaces according to claim 1, wherein said composite film is prepared by: placing core substance particles at a regular interval on one film obtained by forming a liquid containing a polymerizable monomer into a liquid film and then subjecting the same to polymerization; laminating said one film and other film obtained by forming a liquid containing a polymerizable monomer into a liquid film and then subjecting the same to polymerization; and subjecting the films thus laminated to further polymerization. ### Claim 8 (depends on 7) The process for production of composite fine particles with heterogeneous surfaces according to claim 7, wherein said core substance particles are placed on said one film through an ink-jet method. ### Claim 9 (depends on 7) The process for production of composite fine particles with heterogeneous surfaces according to claim 7, wherein said composite film is cut into minute pieces with said core substance particles being located in central portions thereof. ### Claim 10 A process for production of composite fine particles with heterogeneous surfaces comprising: forming a liquid containing a polymerizable monomer and a white pigment into a liquid film and then subjecting the same to polymerization to obtain a first film; forming a liquid containing a polymerizable monomer and a black pigment into a liquid film and then subjecting the same to polymerization to obtain a second film; laminating the films to prepare a composite film; subjecting the composite film to further polymerization; a step of cutting the composite film into minute pieces; and a step of melting said minute pieces. ### Claim 11 A process for production of composite fine particles with heterogeneous surfaces comprising: forming a liquid containing a hydrophobic polymerizable monomer into a liquid film and then subjecting the same to polymerization to form a first film; forming a liquid containing a hydrophilic polymerizable monomer into a liquid film and then subjecting the same to form a second film; laminating the films to prepare a composite film; subjecting the composite film to further polymerization; a step of cutting the composite film into minute pieces; and a step of melting said minute pieces.