# US 8,771,412 B2 · Refractory coating for producing mold coatings > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 8,771,412 B2 - Document ID: US8771412B2 - Status: Granted - Kind: B2 - Application number: 13/383,169 - Filed: 2010-04-21 - Published: 2012-05-24 - Granted: 2014-07-08 - Earliest claimed: 2009-07-09 - Assignees: HüTtenes-Albertus Chemische Werke Gesellschaft Mit BeschräNkter Haftung - Applicants: Andreas Stefan Jattke; Günter Thomas Linke; Klaus Seeger - Inventors: Andreas Stefan Jattke; Günter Thomas Linke; Klaus Seeger - Web page: https://patentgrep.com/patent/US8771412B2 ## CPC - B22C 3/00: Selection of compositions for coating the surfaces of moulds, cores, or patterns - B22C 1/14: for separating the pattern from the mould - B22C: FOUNDRY MOULDING (moulding refractory materials in general B28B) ## Abstract The present invention relates to a refractory coating for producing mold coatings by application to inorganically or organically-bound molding materials in lost molds or to cores for iron and steel casting, wherein the ready-to-use refractory coating has proportion by weight of 0.001% or more and less than 1% of inorganic hollow bodies, which partially or fully consist of crystalline material and have a softening point of 1000° C. or higher. ## Claims ### Claim 1 A refractory wash for producing mold coatings on lost molds or to cores for iron and steel casting, wherein the refractory wash contains a proportion by weight of 0.001% through 0.99% of inorganic hollow bodies, characterized in that wherein the inorganic hollow bodies in part or in full consist of comprise a crystalline material, wherein the refractory wash comprises: (a) 0.0011 to 3.5 parts by weight of inorganic hollow bodies, which partially or fully consist of crystalline material; (b) 20 to 75 parts by weight of one or a plurality of refractory materials, which are not hollow bodies as defined under (a); (c) at least 15 parts by weight of at least one carrier fluid; (d) 0.1 to 10 parts by weight of one or a plurality of suspending agents; (e) 0.01 to 0.6 parts by weight of one or a plurality of biocides; (f) 0 to 4 parts by weight of one or a plurality of wetting agents; (g) 0 to 2 parts by weight of one or a plurality of floating agents and/or rheological additives; and (h) 0 to 2 parts by weight of one or a plurality of binding agents. ### Claim 2 (depends on 1) The refractory wash as claimed in claim 1, characterized in that the said inorganic hollow bodies have a softening point of 1000° C. or higher. ### Claim 3 (depends on 1) The refractory wash as claimed in claim 1, characterized in that said inorganic hollow bodies consist of silicates, or oxides, or carbides, or nitrides, or mixtures of these materials, or mixtures of inorganic hollow bodies of these materials. ### Claim 4 (depends on 1) The refractory wash as claimed in claim 1, wherein the inorganic hollow bodies are hollow balls with a diameter of less than 400 μm. ### Claim 5 (depends on 1) The refractory wash as claimed in claim 1, characterized in that the inorganic hollow bodies have a cavity that accounts for 15% or more of the volume of a three-dimensional structure of the inorganic hollow bodies. ### Claim 6 (depends on 1) The refractory wash as claimed in claim 1, characterized in that the inorganic hollow bodies have compressive strengths of 10 MPa or higher. ### Claim 7 (depends on 1) The refractory wash as claimed in claim 1, characterized in that the inorganic hollow bodies are hollow balls with an external diameter of 10 through 150 μm. ### Claim 8 (depends on 1) The refractory wash as claimed in claim 1, characterized in that the inorganic hollow bodies have a hardness of 5 through 6 on the Mohs scale. ### Claim 9 (depends on 1) The refractory wash as claimed in claim 1, characterized in that the inorganic hollow bodies have a compressive strength of more than 25 MPa. ### Claim 10 (depends on 1) The refractory wash as claimed in claim 1, characterized in that the inorganic hollow bodies are hollow balls with a cavity that accounts for 70% or more of the total volume of the hollow ball. ### Claim 11 (depends on 1) The refractory wash as claimed in claim 1, characterized in that a plurality of the inorganic hollow bodies are hollow balls with an external diameter in the range 10 through 150 μm; a cavity that accounts for 70% or more of the total volume of the hollow ball; a softening point of 1200° C. through 1450° C.; a hardness of 5 through 6 on the Mohs scale; and a compressive strength of 25 MPa or higher. ### Claim 12 (depends on 1) The refractory wash as claimed in claim 1, characterized in that the inorganic hollow bodies are hollow balls according to CAS-No. 93924-19-7 (cenospheres), which form during combustion of coal at power stations as part of fly ash associated with the combustion and are separated from exhaust gas flow associated with the combustion. ### Claim 13 (depends on 1) The refractory wash as claimed in claim 1, characterized in that the inorganic hollow bodies consist of carbon or are mixtures of inorganic hollow bodies of carbon and inorganic hollow bodies of one or a plurality of materials selected from the group consisting of silicates, oxides, carbides, nitrides mixtures of these materials, or mixtures of inorganic hollow bodies of these materials. ### Claim 14 (depends on 13) The refractory wash according to claim 13, characterized in that the inorganic hollow bodies of carbon comprise nano hollow bodies of carbon. ### Claim 15 (depends on 1) The refractory wash as claimed in claim 1, wherein the refractory wash is a mixture comprising (1) a first fluid carrier, and (2) a base composition, wherein said base composition comprises: (a) 0.0011 to 3.5 wt-% of inorganic hollow bodies, which partially or fully consist of crystalline material; (b) 20 to 75 wt-% of one or a plurality of refractory materials, which are not hollow bodies as defined under (a); (c) 15 to 80 wt-% of at least one carrier fluid; (d) 0.1 to 10 wt-% of one or a plurality of suspending agents; (e) 0.01 to 0.6 wt-% of one or a plurality of biocides; (f) 0 to 4 wt-% of one or a plurality of wetting agents; (g) 0 to 2 wt-% of one or a plurality of floating agents and/or rheological additives; (h) 0 to 2 wt-% of one or a plurality or binding agents, wherein the amounts of components (a)-(h) are relative to the total weight of the base composition. ### Claim 16 (depends on 1) A method of producing a coating on a mold or a core for use in casting, comprising applying a refractory wash as claimed in claim 1 to a mold or a core for use in casting. ### Claim 17 (depends on 1) The method for producing a coating on the basis of a refractory coating on a mold or core comprising the following steps: producing or providing of a mold or core to be coated; providing a refractory as defined in claim 1; applying the refractory wash to the core or the mold so that a coating on the basis of a refractory coating results with a thickness of 0.05 mm or higher. ### Claim 18 (depends on 17) The method according to claim 17, characterized in that the application of the refractory wash takes place by a method from the group consisting of immersing, flooding, spraying and painting of the mold or of the core. ### Claim 19 (depends on 17) The method according to claim 17, characterized in that drying of the refractory coating takes place by application of heat or microwave radiation.