Spinel-germanate glass composite as an IR window
AssigneeThe United States of America as represented by the Secretary of the Navy
InventorsShyam S. Bayya, Jasbinder S. Sanghera, Guillermo R. Villalobos, Ishwar D. Aggarwal
Life of this patent
Estimating the term…
Abstract
This disclosure involves a new spinel and glass micro-composite material and process for making such. The composite has excellent transmission in the 0.5-5.0 μm wavelength region suitable for various visible and mid IR applications utilizing windows, domes and other geometric shapes. The composite can be made at a temperature about 40% lower than the glass melting temperature and about 50% lower than the spinel sintering temperature. The composite material has high modulus and fracture toughness which are important for impact resistance in armor and other practical applications.
Claims8
A method of making spinel-germanate glass composite comprising:
- melting a germanate glass in a crucible in the temperature range of about 1300° C.-1350° C.;
- powdering and sieving the germanate glass through 325 and 400 size mesh;
- collecting the germanate glass powders in the range of 37-44 μm;
- sintering a spinel powder to form spinel powders;
- powdering and sieving the spinel powders through 325 and 400 size mesh;
- collecting the spinel powders of particle size about 37-44 μm;
- mixing the germanate glass powders and the spinel powders so that the resulting mixed powders contain 0.0001 to 40% volume fraction of the spinel powders;
- loading the mixed powders in a die;
- hot pressing the mixed powders in the die in the temperature range of about 650° C. to 800° C. and pressure in the range of about 1,000 to 10,000 psi for about 30 minutes to about 6 hours;
- and
- cooling the mixed powders to form a spinel-germanate glass composite.
A method of making spinel-germanate glass composite comprising:
- preparing a 15BaO-15Ga2O3-70GeO2 glass batch;
- mixing the glass batch for about 30 minutes;
- transferring the glass batch to a platinum crucible;
- placing the platinum crucible containing the glass batch in a pre-melting furnace preheated to 1350° C.;
- allowing the glass batch to melt;
- quenching in air to make a cullet;
- transferring the cullet to another crucible that was loaded in a sealed atmosphere controlled furnace;
- flushing the furnace with dry argon for about 1 hour to remove moist air;
- heating the furnace to about 1300° C. under Ar/O2 atmosphere;
- bubbling the glass batch using a bubbling tube with Ar/O2 mixture mixed in 80:20 ratio for about 9 hours;
- removing the bubbling tube;
- maintaining the temperature of about 1300° C. for another about 30 minutes with the O2/Ar gasses still flowing;
- quenching in the sealed furnace and cooling to room temperature;
- crushing, grounding and sieving through 325 and 400 size mesh to collect glass powder in the size range of 37-44 μm;
- milling and sieving spinel powder through 325 and 400 size mesh to collect powder in the size range of 37-44 μm;
- mixing the glass batch and the spinel powder;
- and
- hot pressing in a graphite die in the temperature range of about 700-780 C for about 2 hours at about 1500 psi pressure.
Dependencies are inferred from the claim text.