Film and method of manufacturing the same, laminated film or sheet, and laminated body
AssigneeMitsubishi Rayon Co., Ltd.
InventorsYuhei Konokawa, Yoshinori Abe
Life of this patent
Estimating the term…
Abstract
Provided is a film having high crystallinity, transparency, and surface smoothness, a lamination of the film, a sheet of the film, and a laminated body. A film contains vinylidene fluoride-based resin (A) and acrylic-based resin (B). The film has at least one surface with arithmetic mean roughness of 0.1 to 20 nm. The at least one surface has crystal fusion heat of 18 to 40 J/g and a haze value of 3.5 or less, the crystal fusion heat being measured using a differential scanning calorimeter.
Claims14
A film containing vinylidene fluoride-based resin (A) and acrylic-based resin (B), wherein the film has at least one surface with arithmetic mean roughness of 0.1 to 20 nm,
- the film having crystal fusion heat of 18 to 40 J/g and a haze value of 3.5 or less, and the crystal fusion heat being measured using a differential scanning calorimeter.
A method of manufacturing a film containing vinylidene fluoride-based resin (A) and acrylic-based resin (B), wherein the film has at least one surface with arithmetic mean roughness of 0.1 to 20 nm, the film having crystal fusion heat of 18 to 40 J/g and a haze value of 3.5 or less, and the crystal fusion heat being measured using a differential scanning calorimeter, comprising:
- melt-extruding a resin composition containing 75 to 95% by mass of the vinylidene fluoride-based resin (A) and 5 to 25% by mass of the acrylic-based resin (B),
- wherein the vinylidene fluoride-based resin (A) has a melt mass-flow rate equal to or more than 10 [g/10 minutes], and
- the melt mass-flow rate is measured in compliance with JISK7210 under conditions of 230° C. and a load of 3.8 kg.
A method of manufacturing a film, comprising
- melt-extruding a resin composition containing 75 to 95% by mass of vinylidene fluoride-based resin (A) and 5 to 25% by mass of acrylic-based resin (B), and
- subsequently bringing the obtained melt extrudate into contact with at least one chill roll having the surface temperature of 35 to 75° C.,
- wherein the vinylidene fluoride-based resin (A) has a melt mass-flow rate equal to or more than 10 [g/10 minutes] minutes, and
- the melt mass-flow rate is measured in compliance with JISK7210 under conditions of 230° C. and a load of 3.8 kg.