Low resistance tunneling magnetoresistive sensor with natural oxidized double MgO barrier

Abstract

A high performance TMR sensor is fabricated by incorporating a tunnel barrier having a Mg/MgO/Mg configuration. The 4 to 14 Angstroms thick lower Mg layer and 2 to 8 Angstroms thick upper Mg layer are deposited by a DC sputtering method while the MgO layer is formed by a NOX process involving oxygen pressure from 0.1 mTorr to 1 Torr for 15 to 300 seconds. NOX time and pressure may be varied to achieve a MR ratio of at least 34% and a RA value of 2.1 ohm-um2. The NOX process provides a more uniform MgO layer than sputtering methods. The second Mg layer is employed to prevent oxidation of an adjacent ferromagnetic layer. In a bottom spin valve configuration, a Ta/Ru seed layer, IrMn AFM layer, CoFe/Ru/CoFeB pinned layer, Mg/MgO/Mg barrier, CoFe/NiFe free layer, and a cap layer are sequentially formed on a bottom shield in a read head.