Method of producing a material composite
AssigneePlansee SE
InventorsBertram Schedler, Thomas Huber, Thomas Friedrich, Dietmar Schedle, Anton Zabernig, Karlheinz Schreiber, Hans-Dieter Friedle
Life of this patent
Estimating the term…
Abstract
A material composite has at least one region of copper or a copper alloy, at least one region of a predominantly graphitic material, and at least one boundary region between them. The boundary region has one or more carbides from the group of the IVb, Vb, VIb transition metals and one or more elements of the group consisting of Si, B, Al, Ge, Mn, Sn. In a preferred implementation of the invention, the composite is produced with a back-casting process.
Claims7
A method of producing a material composite, the method which comprises:
- heating copper to a temperature above a melting point thereof, or heating a copper alloy to a temperature above a solidus temperature thereof;
- bringing the copper or copper alloy into contact with a predominantly graphitic material, wherein amounts of one or more elements of the group consisting of Si, B, Al, Ge, Sn, Mn and amounts of one or more elements of the group of the IVb, Vb, VIb transition metals, and a carbide or mixed carbide of one or more elements selected from the group consisting of Si, B, Al, Ge, Sn, Mn are made available in a boundary region during the joining process;
- subsequently cooling to solidify the copper or the copper alloy;
- and
- causing at least one carbide to form islets in the boundary region.
A method of producing a material composite, the method which comprises:
- heating copper to a temperature above a melting point thereof, or heating a copper alloy to a temperature above a solidus temperature thereof;
- bringing the copper or copper alloy into contact with a predominantly graphitic material, wherein amounts of one or more elements of the group consisting of Si, B, Al, Ge, Sn, Mn and amounts of one or more elements of the group of the IVb, Vb, VIb transition metals, and a carbide or mixed carbide of one or more elements selected from the group consisting of Si, B, Al, Ge, Sn, Mn are made available in a boundary region during the joining process;
- subsequently cooling to solidify the copper or the copper alloy;
- applying amounts of one or more elements of the group consisting of Si, B, Al, Ge, Sn, Mn in at least one of elemental form, compound form, and alloy form to the predominantly graphitic material, heating the thus-treated graphitic material to a temperature above a solidus temperature of the elemental, compound, and/or alloy form to cause at least partial wetting of the predominantly graphitic material;
- subsequently applying one or more foils of one or more elements of the group of the IVb, Vb, VIb transition metals to the graphitic material and heating the one or more foils together with the graphitic material to a temperature causing carbide formation;
- and
- covering a treated surface of the graphitic material with copper or a copper alloy in a mold made of a heat-resistant material and heating the complete composite to a temperature above the liquidus temperature of the copper or copper alloy.
A method of forming a component of a fusion reactor, the method which comprises:
- a) producing a material composite by:
- heating copper to a temperature above a melting point thereof, or heating a copper alloy to a temperature above a solidus temperature thereof;
- bringing the copper or copper alloy into contact with a predominantly graphitic material, wherein amounts of one or more elements of the group consisting of Si, B, Al, Ge, Sn, Mn and amounts of one or more elements of the group of the IVb, Vb, VIb transition metals, and a carbide or mixed carbide of one or more elements selected from the group consisting of Si, B, Al, Ge, Sn, Mn are made available in a boundary region during the joining process;
- subsequently cooling to solidify the copper or the copper alloy;
- and
- causing at least one carbide to form islets in the boundary region;
- and
- b) forming the material composite into a cooling element.