# US 8,541,537 B2 · Branched polycarbonate resin and process for producing the same

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 8,541,537 B2
- Document ID: US8541537B2
- Status: Granted
- Kind: B2
- Application number: 13/499,789
- Filed: 2010-10-05
- Published: 2012-10-04
- Granted: 2013-09-24
- Earliest claimed: 2009-10-07
- Assignees: Teijin Chemicals, Ltd.
- Applicants: Takayuki Ozaki; Hiroshi Okamoto; Hiroshi Shuto
- Inventors: Takayuki Ozaki; Hiroshi Okamoto; Hiroshi Shuto
- Web page: https://patentgrep.com/patent/US8541537B2

## CPC

- C08G 64/14: containing a chain-terminating or -crosslinking agent
- C08G: MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS

## Abstract

This invention provides a branched polycarbonate resin obtained from a dihydric phenol compound, a branching agent, monohydric phenols and phosgene by an interfacial polymerization reaction method in the presence of an alkali aqueous solution and an organic solvent, the branched polycarbonate resin having features that: (i) the branching agent content (X) thereof is over 0.70 mol % but 1.50 mol % or less, (ii) the branching agent content (X) and the melt tension (Y) thereof at 280° C. satisfy the following expression (1), 3.8X−2.4≦Y≦3.8X+4.5 (1), and (iii) the entire N content in the branched polycarbonate resin is 0 to 7 ppm.

## Claims

### Claim 1

A branched polycarbonate resin obtained from a dihydric phenol compound, a branching agent, monohydric phenols and phosgene by an interfacial polymerization reaction method in the presence of an alkali aqueous solution and an organic solvent,
wherein the dihydric phenol compound is 2,2-bis(4-hydroxyphenyl)propane, and
wherein, for the branched polycarbonate resin:
(i) the branching agent content (X) thereof is over 0.70 mol % but 1.50 mol % or less,
(ii) the branching agent content (X) and the melt tension (Y) thereof at 280° C. satisfy the following expression (1),
3.8X−2.4≦Y≦3.8X+4.5 (1),
and
(iii) the entire N content in the branched polycarbonate resin is 0 to 7 ppm, and
(iv) the branched polycarbonate resin has a viscosity average molecular weight in the range of 1.8×104 to 3.2×104.

### Claim 2 (depends on 1)

The branched polycarbonate resin of claim 1, wherein the branching agent is a compound formed by substituting 3 or more hydroxyphenyl groups on an alkane having 2 to 8 carbon atoms.

### Claim 3 (depends on 1)

The branched polycarbonate resin of claim 1, wherein the monohydric phenols are compounds selected from the group consisting of p-tert-butylphenol, p-tert-octylphenol, p-cumylphenol, 4-hydroxybenzophenone and phenol.

### Claim 4 (depends on 1)

A process for producing the branched polycarbonate resin of claim 1, which comprises the steps of
(i) blowing phosgene into an alkali aqueous solution containing a dihydric phenol compound and a branching agent in the presence of an organic solvent to allow them to react and thereby obtaining a solution containing a polycarbonate oligomer, wherein the dihydric phenol compound is 2,2-bis(4-hydroxyphenyl)propane,
(ii) charging monohydric phenols into the thus-obtained solution to emulsify the solution, and
(iii) polymerizing the emulsified solution without stirring.

### Claim 5 (depends on 4)

The production process of claim 4, wherein the branching agent is a compound formed by substituting 3 or more hydroxyphenyl groups on an alkane having 2 to 8 carbon atoms.

### Claim 6 (depends on 4)

The production process of claim 4, wherein the monohydric phenols are compounds selected from the group consisting of p-tert-butylphenol, p-tert-octylphenol, p-cumylphenol, 4-hydroxybenzophenone and phenol.