US 8,524,815 B2 · Non halogen flame retardant thermoplastic polyurethane

Abstract

Flame retardant thermoplastic polyurethane (TPU) compositions are disclosed having a flame retardant package comprising an organo-phosphinate component, an organo-phosphate component, and a polyhydric alcohol. The flame retardant components may be present in an amount from about 5 to about 40 weight percent of the phosphinate compound; from about 5 to about 20 weight percent of the phosphate compound, and from about 0.1 to about 15 weight percent of the polyhydric alcohol, based on the total weight of the TPU composition. Processes are disclosed to make the TPU compositions and to make wire and cable constructions employing the TPU compositions as the jacket of the wire and cable constructions. The TPU compositions exhibit excellent flame retardant capabilities as measured by Limited Oxygen Index testing and/or UL 94 Vertical Burn tests.

Claims10

Dependent claims

A flame retardant thermoplastic polyurethane composition having good melt processing characteristics comprising:

(a) at least one thermoplastic polyurethane polymer;
wherein said thermoplastic polyurethane is formed by the reaction of:
(i) hydroxyl terminated intermediate,
(ii) aromatic diisocyanate, and
(iii) glycol chain extender;
(b) from about 15 to about 25 weight percent of a first organic non-halogenated flame retardant component comprising a phosphinate compound;
(c) from about 5 to about 10 weight percent of a second organic non-halogenated flame retardant component comprising a phosphate compound;
(d) from about 2.5 to about 10 weight percent of a third organic non-halogenated flame retardant component selected from pentaerythritol and dipentaerythritol;
and
(e) talc;
wherein the weight percents are based on the total weight of the thermoplastic polyurethane composition, and wherein said flame retarded thermoplastic polyurethane has a VO rating at 1.90 mm thickness as measured according to UL 94 vertical burn test and a Limited Oxygen Index of at least about 35 as measured according to ASTM D2863.

8 more elements

Dependencies are inferred from the claim text.

Non halogen flame retardant thermoplastic polyurethane

Life of this patent

Non halogen flame retardant thermoplastic polyurethane

Life of this patent