AssigneesNational Institute for Materials Science, Japan Science and Technology Corporation, Anelva Corporation
InventorsIsao Nakatani, Kimiko Mashimo, Naoko Matsui
Life of this patent
Estimating the term…
Abstract
The object of the present invention is to provide a masking material for dry etching, which is suitable for fine processing of a magnetic film as thin as a few nm such as NiFe or CoFe constituting a TMR film and capable of simplifying the process for producing a TMR element and reducing production costs related to facilities and materials. This object was solved by a masking material for dry etching of a magnetic material by using a mixed gas of carbon monoxide and a nitrogenous compound as etching gas, which comprises a metal (tantalum, tungsten, zirconium or hafnium) with a melting or boiling point increasing upon conversion thereof into a nitride or carbide.
Claims2
A method for producing a tunneling magnetoresistive element having a tunneling magnetoresistive structure which comprises an insulating layer sandwiched between two ferromagnetic layers of a pin layer and a free layer, wherein the tunneling magnetoresistive structure has a protective film formed thereon,
- the method comprising:
- forming a mask on a surface of a laminate of the tunneling magnetoresistive structure, wherein the mask comprises a tantalum metal having a specific physical property that its melting point or boiling point increases when the tantalum metal is converted into a nitride or carbide;
- and
- dry etching the laminate, the mask being formed on the surface thereof, using a mixed gas comprising carbon monoxide and a nitrogenous compound as etching gas to form the tunneling magnetoresistive structure;
- wherein the mask including tantalum remains on the surface of the tunneling magnetoresistive structure after the dry etching, and the mask including tantalum is configured to be the protective film of the tunneling magnetoresistive structure after the dry etching.
A method for producing a tunneling magnetoresistive element having a tunneling magnetoresistive structure which comprises an insulating layer sandwiched between two ferromagnetic layers of a pin layer and a free layer, wherein the tunneling magnetoresistive structure has a protective film formed thereon,
- the method comprising:
- forming a mask on a surface of a laminate of the tunneling magnetoresistive structure, wherein the mask comprises a tantalum metal having a specific physical property that its melting point or boiling point increases when the tantalum metal is converted into a nitride or carbide;
- and
- dry etching the laminate, the mask being formed on the surface thereof, using a mixed gas comprising carbon monoxide, a nitrogenous compound and a gas selected from the group consisting of argon, helium, xenon, krypton and neon as etching gas to form the tunneling magnetoresistive structure;
- wherein the mask including tantalum remains on the surface of the tunneling magnetoresistive structure after the dry etching, and the mask including tantalum is configured to be the protective film of the tunneling magnetoresistive structure after the dry etching.