Low temperature co-fired ceramics with low dielectric loss for millimeter-wave application

Abstract

Provided is a dielectric ceramic composition comprising: 40-70 wt % of a borosilicate-based glass frit comprising 50-80 mol % of SiO2, 15-20 mol % of B2O3, 0.1-5 mol % of one or more alkali metal oxide selected from Li2O and Na2O, and 0.1-30 mol % of one or more alkaline earth metal oxide selected from MgO, CaO, SrO and ZnO; and 30-60 wt % of a ceramic filler represented by Chemical Formula 1: (Zn1-xMgx)2SiO4  (1) wherein 0≦x≦1. The disclosed low temperature co-fired ceramic (LTCC) composition is sinterable at low temperature, with a relative density of at least 95% in the temperature range of 800-900° C., is capable of minimizing electric loss, with a dielectric constant of 4-7 and a very low dielectric loss, and is applicable from the low-frequency band to the millimeter-wave band of 60 GHz or more.