Molding composition and method using same to form displacements for use in a metal casting process
AssigneeDestech Corporation
InventorDavid A. Rohrbacker
Life of this patent
Estimating the term…
Abstract
A method to form a displacement for use in a metal casting process, wherein the method provides a plurality of ceramic particles and a plurality of resin particles. The method grinds the plurality of ceramic particles until those ceramic particles comprise diameters less than 150 microns, and grinds the plurality of resin particles until those resin particles comprise diameters less than 100 microns, and forms a powder blend comprising the plurality of ground ceramic particles and the plurality of ground resin particles. The method then disposes the powder blend into a mold comprising a cavity defining the desired displacement. The method further densifies the blend, and cures the resin to form the displacement.
Claims18
A method to form a cutting bit displacement for use in a metal casting process, comprising:
- providing a plurality of ceramic particles;
- providing a plurality of resin particles;
- grinding said plurality of ceramic particles until said ceramic particles comprise diameters less than 150 microns;
- grinding said plurality of uncured resin particles until said resin particles comprise diameters less than 100 microns;
- forming a powder blend comprising said plurality of ground ceramic particles and said plurality of ground resin particles;
- disposing said powder blend into a mold comprising a cavity defining said nozzle displacement;
- densifying said blend;
- heating said mold at a temperature of about 100° C. for about one hour and then at a temperature of about 200° C. for about one hour to crosslink said resin to form said cutting bit displacement.
A method to form a nozzle displacement, comprising:
- providing a plurality of ceramic particles;
- providing a plurality of resin particles;
- providing a plurality of reinforcing fibers;
- grinding said plurality of uncured resin particles until said resin particles comprise diameters less than 100 microns;
- grinding said plurality of uncured resin particles under said resin particles comprise diameters less than 100 microns;
- forming a powder blend comprising said plurality of ground ceramic particles and said plurality of ground resin particles;
- disposing said powder blend into a mold comprising a cavity defining said nozzle displacement;
- densifying said blend;
- heating said mold at a temperature of about 100° C. for about one hour and then at a temperature of about 200° C. for about one hour to crosslink said resin to form said cutting bit displacement.
A method to form a nozzle displacement comprising a graphite core and a ceramic overcoat, comprising:
- providing a plurality of ceramic particles;
- providing a plurality of resin particles;
- providing a cylindrical graphite member;
- grinding said plurality of ceramic particles until said ceramic particles comprise diameters less than 150 microns;
- grinding said plurality of resin particles under said resin particles comprise diameters less than 100 microns;
- forming a powder blend comprising said plurality of ceramic particles and said plurality of resin particles;
- disposing said cylindrical graphite member into a mold comprising a cavity defining said nozzle displacement;
- disposing said powder blend into said mold such that said cylindrical graphite member is partially encapsulated by said powder blend;
- densifying said blend;
- curing said resin to form said nozzle displacement.