# US 8,464,558 B2 · Glass making method > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 8,464,558 B2 - Document ID: US8464558B2 - Status: Granted - Kind: B2 - Application number: 12/524,047 - Filed: 2008-01-25 - Published: 2010-04-29 - Granted: 2013-06-18 - Earliest claimed: 2007-01-26 - Assignees: Saint-Gobain Emballage - Applicants: Sylvie Abensour; Bertrand Maquin - Inventors: Sylvie Abensour; Bertrand Maquin - Web page: https://patentgrep.com/patent/US8464558B2 ## CPC - C03C 3/087: containing calcium oxide, e.g. common sheet or container glass - C03C 1/10: to produce uniformly-coloured transparent products - C03C 4/02: for coloured glass - C03C: CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS ## Abstract The subject of the invention is a process for manufacturing red glass containing copper that comprises the steps consisting in: obtaining a mass of colorless molten glass, free of sulfides, the iron oxide weight content of which is between 0.01 and 0.15%; then conveying said mass of molten glass in a feeder channel, in which copper oxide and tin oxide are added to said mass of molten glass, the partial pressure of oxygen in said mass of molten glass being between 10−7 and 10−4; then forming glass objects, especially bottles or flasks from said mass of molten glass; then subjecting said glass objects to a heat treatment so as to develop a red tint. ## Claims ### Claim 1 A process for manufacturing red glass comprising copper, the process comprising: (1) obtaining within a glass melting furnace a mass of colorless molten glass formed by melting at least one batch material comprising sand, wherein said mass is free of sulfides, a weight content of iron oxide in said mass is between 0.01 and 0.15%, and a ratio of the weight of sulfate (in SO3 form) of said mass to the weight of sand is between 0.3 and 0.6%; (2) conveying said mass of colorless molten glass, having a partial pressure of oxygen of between 10−7 and 10−4, in a feeder channel; then (3) adding within the feeder channel copper oxide and tin oxide to said mass of colorless molten glass to form a copper-containing molten glass, such that a partial pressure of oxygen in said mass of colorless molten glass within the feeder channel is between 10−7 and 10−4; (4) forming a glass object from said copper-containing molten glass; then (5) heat treating said glass object to develop a red tint and to form a red glass object. ### Claim 2 (depends on 1) The process according to claim 1, wherein the mass of colorless molten glass is obtained by mixing batch materials comprising sand, limestone, sodium carbonate and a sulfate. ### Claim 3 (depends on 1) The process according to claim 1, wherein the weight content of iron oxide in the mass of colorless molten glass is between 0.012% and 0.05%. ### Claim 4 (depends on 1) The process according to claim 1, wherein the partial pressure of oxygen in the mass of colorless molten glass conveying (2) within the feeder channel is between 10−6 and 10−4. ### Claim 5 (depends on 1) The process according to claim 1, wherein the copper oxide and the tin oxide are added to the mass of colorless molten glass in the form of at least one glass frit or agglomerate. ### Claim 6 (depends on 5) The process according to claim 5, wherein a total content of the at least one glass frit or agglomerate is less than or equal to 10%, relative to the weight of the mass of colorless molten glass. ### Claim 7 (depends on 5) The process according to claim 5, wherein at least one glass fit or agglomerate comprising copper oxide comprises between 15 and 30% by weight of copper oxide (expressed in the Cu2O form). ### Claim 8 (depends on 5) The process according to claim 5, wherein at least one glass fit or agglomerate comprising copper oxide has a partial pressure of oxygen, measured at a temperature of 1100° C., of between 10−4 and 10−1. ### Claim 9 (depends on 5) The process according to claim 5, wherein at least one glass frit or agglomerate comprising tin oxide comprises between 15 and 30% by weight of tin oxide (expressed in the SnO form). ### Claim 10 (depends on 5) The process according to claim 5, wherein at least one glass frit or agglomerate comprising tin oxide has a partial pressure of oxygen, measured at a temperature of 1100° C., of between 10−9 and 10−7. ### Claim 11 (depends on 5) The process according to claim 5, wherein a total content of the at least one glass frit or agglomerate is less than or equal to 5% relative to the weight of the mass of colorless molten glass. ### Claim 12 (depends on 5) The process according to claim 5, wherein at least one glass frit or agglomerate comprising copper oxide has a partial pressure of oxygen, measured at a temperature of 1100° C., of between 10−4 and 10−2. ### Claim 13 (depends on 1) The process according to claim 1, further comprising adding, within the feeder channel, bismuth oxide (Bi2O3) to the mass of colorless molten glass, said bismuth oxide being in the form of at least one frit or agglomerate. ### Claim 14 (depends on 1) The process according to claim 1, wherein the heat treating is an annealing treatment. ### Claim 15 (depends on 1) The process according to claim 1, wherein the weight content of iron oxide in the mass of colorless molten glass is between 0.015% and 0.05%. ### Claim 16 (depends on 1) The process according to claim 1, wherein the red glass object has a light transmission under illuminant C of between 5% and 30% for a thickness of 3 mm.