Core-shell quantum dot fluorescent fine particles
AssigneeOsaka University
InventorsTakahisa Omata, Shinichi Hashimoto, Katsuhiro Nose, Satoshi Kobayashi, Yuki Iguchi
Life of this patent
Estimating the term…
Abstract
Disclosed is an ultraviolet fluorescent material having high light emission efficiency, wherein the peak wavelength of ultraviolet light to be emitted can be controlled by having a quantum dot structure wherein a fine crystal of zinc oxide having an average diameter of 1-10 nm serves as a core, and the surface of the zinc oxide fine crystal is covered with at least one of LiGaO2, LiAlO2, NaGaO2 and NaAlO2, which has a crystal structure similar to that of the zinc oxide and low lattice mismatch and hardly suffers from structural defects, or a solid solution thereof.
Claims7
Core-shell quantum dot fluorescent fine particles, each having
- a core formed of zinc oxide nanocrystals having average diameter of 1 nm to 7 nm, and ultraviolet fluorescence wavelength of 371 nm or shorter
- a semiconductor shell formed of any of lithium gallium oxide, lithium aluminum oxide, sodium gallium oxide and sodium aluminum oxide, coating the surface of said core;
- wherein
- said core and said semiconductor shell form a type I three-dimensional quantum well.
Core shell quantum dot fluorescent fine particles, each having
- a core formed of zinc oxide nanocrystals having average diameter of 1 nm to 10 nm, and
- a semiconductor shell formed of a solid solution of at least two selected from lithium gallium oxide, lithium aluminum oxide, sodium gallium oxide and sodium aluminum oxide, coating the surface of said core;
- wherein
- energy of the top of the valence band of said semiconductor shell is lower than energy of the top of the valence band of said core, and energy of the bottom of the conduction band of said semiconductor shell is higher than energy of the bottom of the conduction band of said core;
- and
- said core and said semiconductor shell form a type I three-dimensional quantum well.
Core shell quantum dot fluorescent fine particles, each having
- a core formed of zinc oxide nanocrystals having average diameter of 1 nm to 10 nm, and
- a semiconductor shell formed of any of LiGaO2, LiAlO2, NaGaO2 and NaAlO2, coating the surface of said core;
- wherein
- said core and said semiconductor shell form a type I three-dimensional quantum well.
Core shell quantum dot fluorescent fine particles, each having
- a core formed of zinc oxide nanocrystals having average diameter of 1 nm to 10 nm, and
- a semiconductor shell formed of a solid solution of at least two selected from LiGaO2, LiAlO2, NaGaO2 and NaAlO2, coating the surface of said core;
- wherein
- energy of the top of the valence band of said semiconductor shell is lower than energy of the top of the valence band of said core, and energy of the bottom of the conduction band of said semiconductor shell is higher than energy of the bottom of the conduction band of said core;
- and
- said core and said semiconductor shell form a type I three-dimensional quantum well.
Dependencies are inferred from the claim text.