Surface-oxide abrasion-resistant lubricant coating and method for forming the same

A surface-oxide abrasion-resistant lubricant coating formed of two metal oxides that are produced as a result of fine-particle powders of two respective soft metals, each of the soft metals having lower hardness and lower melting point than a base material of a sliding contact portion to be lubricated, the sliding contact portion being adapted to slidingly contact an object to be contacted and where the fine-particle powders are caused to be to be oxidized by colliding the fine-particle powder of the soft metal that becomes a metal oxide with relatively high hardness as a result of oxidation with a compressed gas containing oxygen against the surface of the sliding contact portion and then by colliding the fine-particle powder of the soft metal that becomes a metal oxide with relatively low hardness as a result of oxidation with the compressed gas containing oxygen against the surface of the sliding contact portion such that one of the two metal oxides has higher hardness than the other,

• the surface-oxide abrasion-resistant lubricant coating has a two-layer structure including:
• a high-hardness portion formed of the metal oxide having relatively higher hardness formed over the base material;
• and
• a low-hardness portion formed of the metal oxide having relatively lower hardness formed over the high-hardness portion, and the low-hardness portion having relatively low hardness than the high-hardness portion, and having decreased friction resistance and shear resistance, and shear fractures concentrated to the low-hardness portion, and
• the low-hardness portion having a thickness of 0.1 μm to 2 μm.

A method for forming a surface-oxide abrasion-resistant lubricant coating, the method comprising the steps of:

• providing a compressed gas that contains oxygen;
• colliding a mixed fluid consisting of the compressed gas containing oxygen and fine-particle powders of two respective soft metals each having a lower hardness and lower melting point than a base material of a sliding contact portion to be lubricated against a surface of the sliding contact portion at an ejection pressure of 0.5 MPa or more or at an ejection speed of 200 m/sec or more;
• reacting the fine-particle powders of the two respective soft metals with the oxygen in the compressed gas so as to cause oxidation at the surface of the sliding contact portion to produce two metal oxides, such that one of the two metal oxides has relatively higher hardness than the other;
• and
• forming a surface-oxide abrasion-resistant lubricant coating formed of the two metal oxides,
• the surface-oxide abrasion-resistant lubricant coating including a high-hardness portion and a low-hardness portion which has relatively lower hardness than the high-hardness portion,
• the high-hardness portion being formed at a side of the base material of the sliding contact portion;
• the low-hardness portion with a thickness of 0.1 μm to 2 μm at an interface which is located between the sliding contact portion that contacts the object to be contacted and a side of an object to be contacted and wherein the interface is a surface of the surface-oxide abrasion-resistant lubricant coating,
• the low-hardness portion having decreased friction resistance and shear resistance, and shear fractures concentrated to the low-hardness portion,
• the fine-particle powder of the soft metal that becomes a metal oxide of relatively higher hardness having a particle diameter smaller than the particle diameter of the fine-particle powder of the soft metal that becomes a metal oxide having relatively lower hardness,
• and the ejection speed of the fine-particle powder of the soft metal that becomes the metal oxide having relatively lower hardness is relatively lower than the ejection speed of the fine-particle powder of the soft metal that becomes the metal oxide having relatively higher hardness, and
• the low-hardness portion of the surface-oxide abrasion-resistant lubricant coating being formed of the metal oxides, one of the metal oxides having relatively higher relatively hardness and the other having relatively lower hardness as a result of oxidation during colliding, and
• coverage of the metal oxide with relatively lower hardness at the low-hardness portion being at least 80%.

The method for forming a surface-oxide abrasion-resistant lubricant coating comprising the steps of:

• providing a compressed gas that contains oxygen,
• using the compressed gas containing oxygen to collide a fine-particle powder of a soft metal having lower hardness and lower melting point than a base material of a sliding contact portion to be lubricated against a surface of the sliding contact portion so that it becomes a metal oxide with relatively higher hardness as a result of oxidation at the surface of the sliding contact portion to be lubricated, and at an ejection pressure of 0.5 MPa or more or at an ejection speed of 200 m/sec or more to form a high-hardness portion,
• using the compressed gas containing oxygen to collide a fine-particle powder of a soft metal having lower hardness and lower melting point than the base material of the sliding contact portion to be lubricated against the high-hardness portion so that it becomes a metal oxide with relatively lower hardness as a result of oxidation at the high-hardness portion at an ejection pressure of 0.5 MPa or more or at an ejection speed of 200 m/sec or more to form a low-hardness portion which has relatively lower hardness than the high hardness portion, the lower hardness-portion having a thickness of 0.1 μm to 2 μm, and having decreased friction resistance and shear resistance, and shear fractures concentrated to the low-hardness portion.