Semiconductor light-emitting element, fabrication method thereof, convex part formed on backing, and convex part formation method for backing

A semiconductor light-emitting element fabrication method for a semiconductor light-emitting element, which includes a light-emitting portion formed with a first compound semiconductor layer, an active layer, and a second compound semiconductor layer whose top surface is a {100} face, comprising a step of forming a convex part, which extends in parallel with a <110> direction, on part of the second compound semiconductor layer in a thickness direction thereof, wherein a convex part formation step includes the sub-steps of:

• (a) forming a mask layer, which extends in parallel with the <110> direction, on the top surface of the second compound semiconductor layer;
• (b) etching part of the second compound semiconductor layer in the thickness direction thereof according to a wet etching method, which employs an etching solution, using the mask layer as an etching mask so as to form a convex-part upper layer whose sectional shape on a cutting plane corresponding to a {110} face is an isosceles trapezoid, the base of which is longer than the upper side thereof, and the side surface of which has an inclination of θU;
• and
• (c) etching part of the second compound semiconductor layer in the thickness direction thereof according to the wet etching method at a different temperature of the etching solution and using the mask layer and the side surface of the convex-part upper layer as an etching mask so as to form a convex-part lower layer whose sectional shape on the cutting plane corresponding to the {110} face is an isosceles trapezoid, the base of which is longer than the upper side thereof, and the side surface of which has an inclination of θD (where θD≠θU).

A semiconductor light-emitting element fabrication method comprising the steps of:

• (A) forming a convex part, which extends in parallel with a <110> direction of an element fabrication substrate, on the principal surface of the element fabrication substrate having a {100} face as the principal surface thereof;
• (B) forming a light-emitting portion, which has a first compound semiconductor layer exhibiting a first conductivity type, an active layer, and a second compound semiconductor layer exhibiting a second conductivity type sequentially accumulated, on the top surface of the convex part, and concurrently forming a laminated structure, which has the first compound semiconductor layer exhibiting the first conductivity type, the active layer, and the second compound semiconductor layer exhibiting the second conductivity type sequentially accumulated, on part of the principal surface of the element fabrication substrate on which the convex part is not formed;
• (C) forming a current block layer, which shields at least the side surface of the active layer included in the light-emitting portion, on the laminated structure;
• (D) forming a contact layer on the entire surface of the current block layer, and forming a second electrode on the contact layer;
• (E) bonding the element fabrication substrate to a supporting substrate with the second electrode between them, and removing the element fabrication substrate;
• and
• (F) forming a first electrode electrically connected to the first compound semiconductor layer, wherein the step (A) includes the sub-steps of
• (a) forming a mask layer, which extends in parallel with the <110> direction, on the principal surface of the element fabrication substrate,
• (b) etching the principal surface of the element fabrication substrate according to a wet etching method, which employs an etching solution, using the mask layer as an etching mask so as to form a convex-part upper layer whose sectional shape on a cutting plane corresponding to a {110} face is an isosceles trapezoid, the base of which is longer than the upper side thereof, and the side surface of which has an inclination of θU, and
• (c) further etching the principal surface of the element fabrication substrate according to the wet etching method at a different temperature of the etching solution and using the mask layer and the side surface of the convex-part upper layer as an etching mask so as to form a convex-part lower layer whose sectional shape on the cutting plane corresponding to the {110} face is an isosceles trapezoid, the base of which is longer than the upper side thereof, and the side surface of which has an inclination of θD (where θD≠θU).