Back to results
US 8,366,822 B2Granted
Cementitious tile adhesives and method of applying the same to a tile substrate
AssigneeDow Global Technologies LLC
InventorsLinda H. Kim-Habermehl, Liang Hong
Life of this patent
Estimating the term…
Abstract
Cement tile adhesives and methods for using them, the adhesives comprising a dry mix of a water-redispersible polymer powder made from a low carboxylation, large particle size water-soluble film-forming vinyl aromatic-diene copolymer latex and a reduced amount of cellulose ether exhibit superior water immersion shear strength and freeze/thaw shear strength.
Claims10
A cement containing dry mix composition comprising
- a) hydraulic cement;
- b) a water-redispersible polymer powder (RDP) comprising a water-insoluble film-forming vinyl aromatic-diene polymer and a colloidal stabilizer, said water-insoluble film-forming polymer having an average particle size of from 200 nm to 500 nm and an amount of carboxylation of from 0.1% by weight to 2.25% by weight of at least one ethylenically unsaturated dicarboxylic acid, salts thereof, or mixtures thereof, based on the amount of copolymerized carboxyl group containing monomer based on the total weight of monomers used to make the polymer;
- and,
- c) from 0.17 to 0.35 wt. %, based on the total weight of the dry mix composition of the present invention, of a cellulose ether,
- whereby when the dry mix is mixed with water to form a mortar or adhesive having a mortar viscosity within the range of 400,000 to 600,000 cps mortar at 5 rpm, the amount of cellulose ether used is reduced by at least 15% as compared to the amount of cellulose ether used to achieve the same mortar viscosity when using the same cement comprising the same cellulose ether and the same amount of the same RDP made from the same polymer as the vinyl aromatic-diene latex polymer and having the same average particle size, with the exception that the latex polymer in the comparative composition has a degree of carboxylation of 2.5 wt. %.
2 more elements
A method of sealing, bonding or coating a substrate comprising:
- providing a dry mix cement composition comprising:
- hydraulic cement, a water redispersible vinyl aromatic-diene polymer powder (RDP) comprising a water-insoluble film-forming polymer and a colloidal stabilizer, and an amount of a cellulose ether, said film-forming polymer having an average particle size of from 200 nm to 500 nm and an amount of carboxylation of from 0.1% by weight to lower than 2.25% wt. % of at least one ethylenically unsaturated dicarboxylic acid, salts thereof, or mixture thereof, based on the amount of copolymerized carboxyl group containing monomer based on the total weight of monomers used to make the polymer, wherein the amount of the cellulose ether is reduced by at least 15% as compared to the amount of cellulose ether used to achieve a mortar viscosity within the range of 400,000 to 600,000 cps mortar at 5 rpm when using the same cement comprising the same cellulose ether, and the same amount of the same RDP made from the same polymer as the vinyl aromatic-diene latex polymer and having the same average particle size, with the exception that the latex polymer in the comparative composition has a degree of carboxylation of 2.5 wt. %;
- (1) mixing the dry mix hydraulic cement composition with water to make a mortar having a desired mortar viscosity of from 400,000 to 600,000 cps mortar at 5 rpm,
- (2) applying the mortar to a substrate;
- (3) applying a tile thereto;
- and,
- (4) drying.
4 more elements
Dependencies are inferred from the claim text.