Thin film transistors having multiple doped silicon layers

A thin film transistor fabrication method, comprising:

• depositing an amorphous silicon layer over a substrate having a gate electrode and a gate dielectric layer formed thereon;
• depositing two or more doped silicon layers over the amorphous silicon layer, each doped silicon layer having at least one characteristic that is different than the other doped silicon layers, wherein depositing the two or more doped silicon layers comprises:
• depositing a first doped silicon layer on the amorphous silicon layer under first deposition conditions, wherein the first deposition conditions comprise a deposition rate of between about 1800 Angstroms per minute and about 2200 Angstroms per minute, a deposition time of between about 5 seconds and about 10 seconds to produce a first doped silicon layer having a resistivity of between about 110 Ωcm to about 120 Ωcm;
• and
• depositing a second doped silicon layer on the first doped silicon layer under second deposition conditions different than the first deposition conditions, wherein, the second deposition conditions comprise a deposition rate of between about 280 Angstroms per minute and about 320 Angstroms per minute for a deposition time of between about 10 seconds to about 18 seconds to produce the second doped silicon layer having a resistivity of between about 30 Ωcm to about 40 Ωcm;
• depositing a metal layer over the two or more doped silicon layers;
• patterning the metal layer to form a source electrode and a drain electrode;
• patterning the two or more doped silicon layers to expose the amorphous silicon layer;
• and
• depositing a passivation layer over the source electrode, the drain electrode and the exposed amorphous silicon layer.

A thin film transistor fabrication method, comprising:

• depositing an amorphous silicon layer over a substrate having a gate electrode and a gate dielectric layer formed thereon;
• depositing two or more doped silicon layers over the amorphous silicon layer, each doped silicon layer having at least one characteristic that is different than the other doped silicon layers, wherein depositing the two or more doped silicon layers comprises:
• depositing a first doped silicon layer on the amorphous silicon layer under first deposition conditions;
• and
• depositing a second doped silicon layer on the first doped silicon layer under second deposition conditions different than the first deposition conditions, wherein, the second deposition comprises introducing silane gas at a flow rate of between about 5000 sccm and about 20000 sccm, introducing hydrogen gas at a flow rate of up to about 200000 sccm, introducing 0.5 percent PH3 in H2 at a flow rate of between about 1000 sccm and about 200000 sccm, applying an RF power to a showerhead of between about 500 W and about 15000 W, maintaining a chamber pressure of between about 1 Torr and about 5 Torr and a spacing between the showerhead and the substrate of between about 400 mils and about 1200 mils;
• depositing a metal layer over the two or more doped silicon layers;
• patterning the metal layer to form a source electrode and a drain electrode;
• patterning the two or more doped silicon layers to expose the amorphous silicon layer;
• and
• depositing a passivation layer over the source electrode, the drain electrode and the exposed amorphous silicon layer.

A thin film transistor fabrication method, comprising:

• depositing an amorphous silicon layer over a substrate having a gate electrode and a gate dielectric layer formed thereon;
• depositing two or more doped silicon layers over the amorphous silicon layer, each doped silicon layer having at least one characteristic that is different than the other doped silicon layers, wherein depositing the two or more doped silicon layers comprises:
• depositing a first doped silicon layer on the amorphous silicon layer under first deposition conditions;
• and
• depositing a second doped silicon layer on the first doped silicon layer under second deposition conditions different than the first deposition conditions, wherein the second deposition comprises introducing silane gas at a flow rate of between about 5000 sccm and about 50000 sccm, introducing hydrogen gas at a flow rate of up to about 150000 sccm, introducing 0.5 percent PH3 in H2 at a flow rate of between about 1000 sccm and about 150000 sccm, applying an RF power to a showerhead of between about 10000 W and about 40000 W, maintaining a chamber pressure of between about 1 Torr and about 5 Torr and a spacing between the showerhead and the substrate of between about 400 mils and about 1200 mils;
• depositing a metal layer over the two or more doped silicon layers;
• patterning the metal layer to form a source electrode and a drain electrode;
• patterning the two or more doped silicon layers to expose the amorphous silicon layer;
• and
• depositing a passivation layer over the source electrode, the drain electrode and the exposed amorphous silicon layer.

A thin film transistor fabrication method, comprising:

• depositing an amorphous silicon layer over a substrate having a gate electrode and a gate dielectric layer formed thereon;
• depositing a first doped silicon layer having a first resistivity on the amorphous silicon layer at a first deposition rate, wherein the first doped silicon layer is deposited under first deposition conditions that comprise a deposition rate of between about 800 Angstroms per minute and about 4000 Angstroms per minute, a deposition time of up to about 30 seconds to produce a first doped silicon layer having a resistivity of between about 70 Ωcm to about 300 Ωcm;
• depositing a second doped silicon layer having a second resistivity less than the first resistivity on the first doped silicon layer, the second doped silicon layer deposited at a second deposition rate less than the first deposition rate, wherein the second doped silicon layer is deposited under second deposition conditions that comprise a deposition rate of between about 50 Angstroms per minute and about 800 Angstroms per minute for a deposition time of between about 15 seconds to about 300 seconds to produce the second doped silicon layer having a resistivity of between about 10 Ωcm to about 70 Ωcm;
• depositing a metal layer over the second doped silicon layer;
• patterning the metal layer to form a source electrode and a drain electrode;
• patterning the first doped silicon layer and the second doped silicon layer to expose the amorphous silicon layer;
• and
• depositing a passivation layer over the source electrode, the drain electrode and the exposed amorphous silicon layer.

A thin film transistor fabrication method, comprising:

• depositing an amorphous silicon layer over a substrate having a gate electrode and a gate dielectric layer formed thereon;
• depositing a first doped silicon layer having a first resistivity on the amorphous silicon layer at a first deposition rate, wherein the first doped silicon layer is deposited under first deposition conditions that comprise a deposition rate of between about 1800 Angstroms per minute and about 2200 Angstroms per minute, a deposition time of between about 5 seconds and about 10 seconds to produce a first doped silicon layer having a resistivity of between about 110 Ωcm to about 120 Ωcm;
• depositing a second doped silicon layer having a second resistivity less than the first resistivity on the first doped silicon layer, the second doped silicon layer deposited at a second deposition rate less than the first deposition rate, wherein the second doped silicon layer is deposited under second deposition conditions that comprise a deposition rate of between about 280 Angstroms per minute and about 320 Angstroms per minute for a deposition time of between about 10 seconds to about 18 seconds to produce the second doped silicon layer having a resistivity of between about 30 Ωcm to about 40 Ωcm;
• depositing a metal layer over the second doped silicon layer;
• patterning the metal layer to form a source electrode and a drain electrode;
• patterning the first doped silicon layer and the second doped silicon layer to expose the amorphous silicon layer;
• and
• depositing a passivation layer over the source electrode, the drain electrode and the exposed amorphous silicon layer.

A thin film transistor fabrication method, comprising:

• depositing an amorphous silicon layer over a substrate having a gate electrode and a gate dielectric layer formed thereon;
• depositing a first doped silicon layer having a first resistivity on the amorphous silicon layer at a first deposition rate;
• depositing a second doped silicon layer having a second resistivity less than the first resistivity on the first doped silicon layer, the second doped silicon layer deposited at a second deposition rate less than the first deposition rate, wherein the second doped silicon layer is deposited under deposition conditions that comprise introducing silane gas at a flow rate of between about 5000 sccm and about 20000 sccm, introducing hydrogen gas at a flow rate of up to about 200000 sccm, introducing 0.5 percent PH3 in H2 at a flow rate of between about 1000 sccm and about 200000 sccm, applying an RF power to a showerhead of between about 500 W and about 15000 W, maintaining a chamber pressure of between about 1 Torr and about 5 Torr and a spacing between the showerhead and the substrate of between about 400 mils and about 1200 mils;
• depositing a metal layer over the second doped silicon layer;
• patterning the metal layer to form a source electrode and a drain electrode;
• patterning the first doped silicon layer and the second doped silicon layer to expose the amorphous silicon layer;
• and
• depositing a passivation layer over the source electrode, the drain electrode and the exposed amorphous silicon layer.

A thin film transistor fabrication method, comprising:

• depositing an amorphous silicon layer over a substrate having a gate electrode and a gate dielectric layer formed thereon;
• depositing a first doped silicon layer having a first resistivity on the amorphous silicon layer at a first deposition rate;
• depositing a second doped silicon layer having a second resistivity less than the first resistivity on the first doped silicon layer, the second doped silicon layer deposited at a second deposition rate less than the first deposition rate, wherein the second doped silicon layer is deposited under deposition conditions that comprise introducing silane gas at a flow rate of between about 5000 sccm and about 50000 sccm, introducing hydrogen gas at a flow rate of up to about 150000 sccm, introducing 0.5 percent PH3 in H2 at a flow rate of between about 1000 sccm and about 150000 sccm, applying an RF power to a showerhead of between about 10000 W and about 40000 W, maintaining a chamber pressure of between about 1 Torr and about 5 Torr and a spacing between the showerhead and the substrate of between about 400 mils and about 1200 mils;
• depositing a metal layer over the second doped silicon layer;
• patterning the metal layer to form a source electrode and a drain electrode;
• patterning the first doped silicon layer and the second doped silicon layer to expose the amorphous silicon layer;
• and
• depositing a passivation layer over the source electrode, the drain electrode and the exposed amorphous silicon layer.