NiMnZn based ferrite
AssigneeTDK Corporation
InventorsKentaro Mori, Takuya Aoki
Life of this patent
Estimating the term…
Abstract
A novel NiMnZn-based ferrite which can reduce magnetic loss (core loss) at a high frequency of about 2 MHz or higher and achieve higher saturated magnetic flux density while forming high sintered density is provided. The NiMnZn-based ferrite contains a main component comprising 54.0 to 57.5 mol % of iron oxide in terms of Fe2O3, 2.0 to 7.0 mol % of zinc oxide in terms of ZnO, 0.5 to 4.7 mol % of nickel oxide in terms of NiO, and a remainder of manganese oxide (in terms of MnO); and an accessory component comprising 100 to 1000 ppm by weight of Si in terms of SiO2, 800 to 3000 ppm by weight of Ca in terms of CaCO3, and 520 to 1000 ppm by weight of Nb in terms of Nb2O5 with respect to the main component; while having an average ferrite crystal particle size of 2.1 to 8.5 μm.
Claims8
A NiMnZn-based ferrite containing:
- a main component comprising 54.0 to 57.5 mol % of iron oxide in terms of Fe2O3, 2.0 to 7.0 mol % of zinc oxide in terms of ZnO, 0.5 to 4.7 mol % of nickel oxide in terms of NiO, and a remainder of manganese oxide (in terms of MnO);
- and
- an accessory component comprising 100 to 1000 ppm by weight of Si in terms of SiO2, 800 to 3000 ppm by weight of Ca in terms of CaCO3, and 520 to 1000 ppm by weight of Nb in terms of Nb2O5 with respect to the main component;
- wherein the ferrite has an average ferrite crystal particle size of 2.1 to 8.5 μm.
Dependencies are inferred from the claim text.