Biodegradable film or sheet, process for producing the same, and composition for biodegradable film or sheet
AssigneeNuclear Engineering, Ltd.
InventorsKazuhiko Aoki, Yasuhiro Ikeo
Life of this patent
Estimating the term…
Abstract
The invention provides a biodegradable film or sheet having water resistance and strength sufficiently. Respective components are mixed so as to form a mixture containing 0% by mass or more and 35% by mass or less of starch, 20% by mass or more and 70% by mass or less of protein, 15% by mass or more and 60% by mass or less of cellulose fibers and 1% by mass or more and 15% by mass or less of urea, then adding 10 or more and 100 or less parts by mass of water to 100 parts by mass of the mixture, kneading the mixture sufficiently with a twin-screw mixer or the like, and rolling the kneaded product under heating at about 120° C. to give a film or sheet with several tens μm to about 300 μm in thickness.
Claims4
A process for producing a biodegradable sheet or sheet, comprising the steps of:
- providing a composition consisting of:
- 0% by mass or more and 35% by mass or less of starch,
- 20% by mass or more and 70% by mass or less of protein,
- 15% by mass or more and 60% by mass or more of cellulose fibers,
- 1% by mass or more and 15% by mass or less of urea;
- and
- optionally a coloring agent and/or a stabilizer;
- adding water to the composition;
- kneading the composition after adding water;
- pressing the kneaded composition under heating;
- and
- obtaining a biodegradable film or sheet, wherein the biodegradable sheet or sheet does not include an oil, glycerin and a metal salt.
A process for producing a biodegradable sheet or sheet, comprising the steps of:
- providing a composition consisting of:
- 0% by mass or more and 30% by mass or less of starch,
- 15% by mass or more and 60% by mass or less of protein,
- 10% by mass or more and 40% by mass or less of cellulose fibers,
- 0.75% by mass or more and 12% by mass or less of urea,
- 20% by mass or more and 60% by mass or less of water;
- and
- optionally a coloring agent and/or a stabilizer;
- kneading the composition,
- pressing the kneaded composition under heating;
- and
- obtaining the biodegradable film or sheet, wherein the biodegradable sheet or sheet does not include an oil, glycerin and a metal salt.
A process for producing a biodegradable sheet or sheet, comprising the steps of:
- providing a composition;
- kneading the composition;
- pressing the kneaded composition under heating;
- and
- obtaining a biodegradable film or sheet,
- wherein the biodegradable film or sheet consists of:
- 0% by mass or more and 35% by mass or less of starch,
- 20% by mass or more and 70% by mass or less of protein,
- 15% by mass or more and 60% by mass or more of cellulose fibers,
- 1% by mass or more and 15% by mass or less of urea;
- and
- optionally water, a coloring agent and/or a stabilizer,
- wherein the biodegradable sheet or sheet does not include an oil, glycerin and a metal salt.