Welding electrode with contoured face
AssigneeGM Global Technology Operations LLC
InventorsDavid R Sigler, Michael J Karagoulis
Life of this patent
Estimating the term…
Abstract
A method for welding a plurality of aluminum to aluminum welds and a plurality of steel to steel welds using the same welder includes providing a resistance spot welder with a pair of weld electrodes having an electrode face radius of curvature in the range between 20 mm and 40 mm. The series of aluminum to aluminum welds is first made, and then, after completing the aluminum to aluminum welds, the series of steel to steel welds are made. After completing the steel to steel welds the weld electrodes are cleaned by an abrasive to remove any buildup or contamination of aluminum on the electrodes. In the event the electrodes have mushroomed, then dressing of the electrodes is provided and then the abrasive cleaning is performed to restore the surface texture.
Claims18
A method for welding a plurality of aluminum to aluminum and plurality of steel to steel electric resistance welds using the same welder comprising:
- providing a resistance spot welder with a pair of weld electrodes having an electrode face radius of curvature in the range between 20 millimeters and 40 millimeters and said electrode face being textured with a roughness in the range of 2 micrometers to 50 micrometers;
- first making a series of aluminum to aluminum welds;
- after completing the aluminum to aluminum welds, then making a series of steel to steel welds;
- after completing the steel to steel welds then cleaning the weld electrodes to remove any buildup of aluminum on the electrodes and retexturing the electrode face to the roughness of 2 micrometers to 50 micrometers prior to next beginning a new series of aluminum to aluminum welds.
A method for welding a plurality of aluminum to aluminum and plurality of steel to steel electric resistance welds using the same welder comprising:
- providing a resistance spot welder with a pair of weld electrodes having an electrode face radius of curvature in the range between 20 millimeters and 40 millimeters, said electrode face being textured with a roughness in the range of 2 micrometers to 50 micrometers, the yield strength of the copper electrode being at least 400 MPa, electrodes being of a copper alloy that does not soften at a temperature of 400° C., the electrodes having an electrical conductivity of greater than 80% IACS conductivity and preferably greater than 90% IACS;
- first making the series of aluminum to aluminum welds;
- after completing the aluminum to aluminum welds, then making the series of steel to steel welds;
- after completing the steel to steel welds then cleaning the weld electrodes to remove any buildup of aluminum on the electrodes and retexturing the electrode face to the roughness of 2 micrometers to 50 micrometers prior to next beginning a new series of aluminum to aluminum welds.
Dependencies are inferred from the claim text.