Slurries and methods of making light weight gypsum board
AssigneeUnited States Gypsum Company
InventorsQiang Yu, Weixin D. Song, Michael R. Lynn
Life of this patent
Estimating the term…
Abstract
The invention generally provides gypsum-containing slurries including stucco, naphthalenesulfonate dispersant, and pregelatinized starch. The naphthalenesulfonate dispersant is present in an amount of about 0.1%-3.0% by weight based on the weight of dry stucco. The pregelatinized starch is present in an amount of at least about 0.5% by weight up to about 10% by weight of pregelatinized starch by weight based on the weight of dry stucco in the formulation. Other slurry additives can include trimetaphosphate salts, accelerators, binders, paper fiber, glass fiber, and other known ingredients.
Claims34
A slurry comprising water, stucco, pregelatinized starch, and a naphthalenesulfonate dispersant;
- the pregelatinized starch is present in an amount from about 0.5% to about 10% by weight based on the weight of the stucco, and the naphthalenesulfonate dispersant is present in an amount from about 0.2% to about 3.0% by weight based on the weight of the stucco;
- when the slurry is cast and dried as board, the board has a density of about 34 pcf or less;
- and
- when the slurry is cast and dried as said board that is about 1/2 inch thick, the board has a nail pull resistance of at least about 65 lb, an average core hardness of at least about 11 lb, and an average flexural strength of at least about 36 lb in a machine direction and/or about 107 lb in a cross-machine direction, the nail pull resistance, the core hardness and the flexural strength as determined in accordance with ASTM C473.
A slurry comprising water, stucco, starch, and foam;
- the starch is present in an amount from about 0.5% to about 10% by weight based on the weight of the stucco and effective to increase the average core hardness of the slurry when set as relative to the slurry without the starch when set;
- when the slurry is cast and dried as board, the board has a density from about 24 pcf to about 34 pcf;
- and
- when the slurry is cast and dried as said board that is about 1/2 inch thick, the board has an average core hardness of at least about 11 lb, and at least one of:
- a nail pull resistance of at least about 65 lb, an average flexural strength of at least about 36 lb in a machine direction, and an average flexural strength of at least about 107 lb in a cross-machine direction, the core hardness, the nail pull resistance, and the flexural strength as determined in accordance with ASTM C473.
A method of making a light weight gypsum board, comprising:
- (a) mixing at least water, stucco, pregelatinized starch, and a naphthalenesulfonate dispersant to form a slurry,
- the pregelatinized starch is present in an amount from about 0.5% to about 10% by weight based on the weight of the stucco, and the naphthalenesulfonate dispersant is present in an amount from about 0.2% to about 3.0% by weight based on the weight of the stucco;
- (b) disposing the slurry between a first cover sheet and a second cover sheet to form a panel;
- (c) cutting the panel into a board;
- and
- (d) drying the board;
- such that the dried board has a density of about 34 pcf or less;
- and
- when the dried board is about 1/2 inch thick, the board has a nail pull resistance of at least about 65 lb, an average core hardness of at least about 11 lb, and an average flexural strength of at least about 36 lb in a machine direction and/or about 107 lb in a cross-machine direction, the nail pull resistance, the core hardness and the flexural strength as determined in accordance with ASTM C473.
A method of making a light weight gypsum board, comprising:
- (a) mixing at least water, stucco, starch, and foam to form a slurry, the starch is present in an amount from about 0.5% to about 10% by weight based on the weight of the stucco and effective to increase the average core hardness of the slurry when set as relative to the slurry without the starch when set;
- (b) disposing the slurry between a first cover sheet and a second cover sheet to form a panel;
- (c) cutting the panel into a board;
- and
- (d) drying the board;
- such that the dried board has a density from about 24 pcf to about 34 pcf;
- and
- when the dried board is about 1/2 inch thick, the board has an average core hardness of at least about 11 lb, and at least one of:
- a nail pull resistance of at least about 65 lb, an average flexural strength of at least about 36 lb in a machine direction, and an average flexural strength of at least about 107 lb in a cross-machine direction, the core hardness, the nail pull resistance, and the flexural strength as determined in accordance with ASTM C473.
Dependencies are inferred from the claim text.