Metal mold repair method and metal mold repair paste agent
AssigneeHonda Motor Co., Ltd.
InventorsMichiharu Hasegawa, Noriyuki Miyazaki, Masafumi Nakamura, Naoji Yamamoto, Kazuo Ueda
Life of this patent
Estimating the term…
Abstract
Providing a metal mold repair method and a metal mold repair paste agent which are capable of repairing cracks with simple work. A repair paste agent containing components that become an alloy is directly applied to a surface of a metal mold having a crack so as to cover the crack part, subsequently a surface of the repair paste agent is coated with an oxidation inhibitor and the repair paste agent is made to penetrate the inside of the crack by heating and becomes an alloy, thereby filling up the crack.
Claims1
A paste metal mold repair agent that becomes an alloy by being subjected to a heat treatment after it is charged in a crack occurring in a metal mold, wherein solid components of the metal mold repair paste agent are contained according to the following percentages (mass %):
- Mn (manganese):
- no less than 15% and no more than 20%
- W (tungsten):
- no less than 8% and no more than 15%
- Fe (iron):
- no less than 2% and no more than 12%
- Co (cobalt):
- no more than 7%
- Cr (chrome):
- no more than 7%
- Si (silicon):
- no more than 7%
- C (carbon):
- no more than 2%
- B (boron):
- no more than 2%
- Ni (nickel):
- balance.
Dependencies are inferred from the claim text.