Brominated styrenic polymers and their preparation
AssigneeAlbemarle Corporation
InventorsCharles H. Kolich, Jeffrey Todd Aplin, John F. Balhoff
Life of this patent
Estimating the term…
Abstract
Preparing brominated styrenic polymer by maintaining a mixture formed from (i) brominating agent, (ii) a solvent solution of styrenic polymer, and (iii) aluminum halide catalyst, at −20 to +20° C., and terminating bromination in 20 minutes or less. New brominated anionic styrenic polymers have better melt flow and/or lower initial ΔE values than the best previously-known brominated anionic styrenic polymers. Other features of such new polymers include high thermal stabilities at 320° C. and/or very low initial color values. Brominated styrenic polymers, especially brominated anionic styrenic polymers, are useful as flame retardants for thermoplastic polymers.
Claims24
Brominated anionic styrenic polymer wherein said polymer is formed with a total bromination time of 20 minutes or less and said polymer having (i) a bromine content of at least about 66 wt %, (ii) a GPC weight average molecular weight in the range of about 8000 to about 50,000, (iii) an initial Hunter Solution ΔE Color Value in the range of above zero to about 1.50, and (iv) a reduced percentage of aromatic rings with ortho-bromine substitution as determined by proton NMR so that the brominated anionic styrenic polymer has when molten and under pressure a measurable flow rate that is higher than brominated anionic styrenic polymers that
- (1) are made by polymerization of the same monomer or from the same styrenic monomers in the same proportions using the same kind of anionic polymerization initiator but with a total bromination time of 35 minutes or more;
- (2) have a bromine content above 66 wt % and differ from the bromine content of said brominated anionic styrenic polymer having characteristics (i), (ii), and (iii) by no more than 1.5 wt %;
- and
- (3) have a GPC weight average molecular weight that differs from the average GPC weight average molecular weight of the two brominated anionic styrenic polymers being compared by no more than 7.5%.
Brominated anionic styrenic polymer wherein said polymer is formed with a total bromination time of 20 minutes or less and has a bromine content of at least about 66 wt %, wherein said polymer (i) has an initial Hunter Solution ΔE Color Value in the range of above zero to about 1.50, and wherein said polymer (ii) is one in which the percentage of aromatic rings having ortho bromine atoms thereon as measured by proton NMR is less than the percentage of the aromatic rings having ortho bromine atoms thereon as compared to a comparable brominated anionic styrenic polymer, which
- (1) is formed by bromination of anionic styrenic polymer produced using the same kind of anionic polymerization initiator and the same kind of styrenic monomer composition but with a total bromination time of 35 minutes or more;
- (2) has a bromine content above 66 wt % that differs from the bromine content of the new brominated anionic styrenic polymer of this invention having characteristics (i) and (ii) by no more than 1.5 wt %;
- and
- (3) has a GPC weight average molecular weight that differs from the average GPC weight average molecular weight of the two brominated anionic styrenic polymers being compared by no more than 7.5%;
- and
- wherein the brominated anionic styrenic polymer has, when subjected to the melt flow index test of ASTM Test Method D1238-00 with the extrusion plastometer operated at 2.16 kg applied pressure and at a temperature selected from 220° C., 235° C., or 270° C. exhibits a measurable flow rate that is higher than that of brominated anionic styrenic polymer formed with a total bromination time of 35 minutes or more.
Brominated anionic styrenic polymer wherein said polymer (i) has a bromine content of about 67 to about 70 wt %, (ii) has a GPC weight average molecular weight in the range of about 10,000 to about 30,000, (iii) was formed with a total bromination time of 20 minutes or less, (iv) has a reduced percentage of aromatic rings with ortho-bromine substitution as determined proton NMR so that the brominated anionic styrenic polymer has, when subjected to the melt flow index test of ASTM Test Method D1238-00 with the extrusion plastometer operated at 2.16 kg applied pressure and at a temperature selected from 220° C., 235° C., or 270° C. exhibits a measurable flow rate that is higher than that of a comparable brominated anionic styrenic polymer formed with a total bromination time of 35 minutes or more, and (v) has an initial Hunter Solution ΔE value in the range of up to 1.50, wherein the comparable brominated anionic styrenic polymer
- (1) is made by polymerization of the same monomer or from the same styrenic monomers in the same proportions using the same kind of anionic polymerization initiator, but with a total bromination time of 35 minutes or more;
- (2) has a bromine content above 66 wt % and differ from the bromine content of said brominated anionic styrenic polymer having characteristics (i), (ii), (iii), (iv), and (v) by no more than 1.5 wt %;
- and
- (3) has a GPC weight average molecular weight that differs from the average GPC weight average molecular weight of the two brominated anionic styrenic polymers being compared by no more than 7.5%.
Dependencies are inferred from the claim text.