Compositions of ethylene/vinyl acetate copolymers for heat-sealable easy opening packaging
AssigneeE.I. du Pont de Nemours and Company
InventorsTerrance D. Kendig, Stephen Robert Tanny
Life of this patent
Estimating the term…
Abstract
Disclosed are compositions comprising ethylene/vinyl acetate copolymers, tackifying resins and optionally polyolefins (for example, polyethylene and polypropylene) that provide strong, tight hermetic heat seals with an easily peelable opening feature to fluoropolymers such as polychlorotrifluoroethylene. Also disclosed are multilayer structures and packages comprising these compositions.
Claims16
A package comprising a multilayer structure having an easily peelable opening feature and a tight hermetic seal wherein the multilayer structure comprises at least one polychlorotrifluoroethylene fluoropolymer substrate layer, and wherein the multilayer structure is prepared by a method comprising the steps of:
- A. providing a polychlorotrifluoroethylene fluoropolymer substrate layer;
- B. providing a resin composition that, when tested substantially in accordance with ASTM F 904-98, peels cleanly away from a polychlorotrifluoroethylene fluoropolymer substrate layer, wherein said resin composition consists essentially of:
- (1) from about 10 to about 90 weight %, based on the total weight of said resin composition, of at least one ethylene/vinyl acetate copolymer having a melt flow rate of 0.1 to 40 g/10 minutes, measured in accordance with ASTM D 1238, Condition E, at 190° C., using a 2.16 kg weight;
- (2) from about 5 to about 35 weight %, based on the total weight of said resin composition, of at least one tackifying resin;
- (3) from about 5 to about 45 weight %, based on the total weight of said resin composition, of at least one polyolefin selected from the group consisting of ethylene polymers;
- and
- (4) from 0 to about 30 weight %, based on the total weight of said resin composition, of filler;
- wherein the resin composition has a viscosity at 190° C. of from about 6 g/10 minutes to about 10.3 g/10 minutes as determined according to ASTM D 1238, Condition E, at 190° C., using a 2.16 kg weight, thereby providing a composition having a viscosity sufficiently high to form a sheet or tape when extruded at a temperature of 190° C.;
- C. selecting an additional material selected from the group consisting of polyesters, polyamides, polyolefins, polyethylene vinyl alcohols, polyethylene vinyl acetates, ethylene/acrylic acid copolymers and ionomers thereof, ethylene/methacrylic acid copolymers and ionomers thereof, polyvinyl chloride, polyvinylidene chloride, anhydride-modified polyolefins and mixtures thereof that has a viscosity sufficiently high to form a sheet or tape when extruded at a temperature of 190° C.;
- D. forming a multilayer coextrudate having at least two layers via coextrusion through a single die in the form of a film, a sheet or a tape, wherein i) a first layer of said extrudate comprises said resin composition of step B, ii) a second layer of said extrudate comprises said additional material of step C, and iii) said first layer is an outer layer of said multilayer coextrudate;
- E. contacting said multilayer coextrudate with said polychlorotrifluoroethylene fluoropolymer substrate layer such that said first layer comprising said resin composition of step B is in contact with and adjacent to said polychlorotrifluoroethylene fluoropolymer substrate layer;
- and
- F. applying sufficient heat and pressure for sufficient time to heat-seal said multilayer coextrudate to said polychlorotrifluoroethylene fluoropolymer substrate layer;
- thereby forming a multilayer structure characterized by a tight hermetic seal and easy peelability wherein the coextrudate peels cleanly away from the polychlorotrifluoroethylene substrate leaving the substrate intact.
Dependencies are inferred from the claim text.