Erosion- and impact-resistant coatings

Abstract

Erosion- and impact-resistant ceramic coatings suitable for protecting surfaces subjected to collisions with particles, including nominally round particles that typically inflict impact damage and more aggressive irregular-shaped particles that typically inflict erosion damage. The ceramic coating is formed to have one of three compositions: at least one layer of titanium aluminum nitride (TiAlN) having a thickness of about 25 to about 100 micrometers; multiple layers of chromium nitride (CrN) and TiAlN, each layer having a thickness of about 0.2 to about 1.0 micrometers to yield a total coating thickness of at least about 3 micrometers; and at least one layer of titanium silicon carbonitride (TiSiCN) having a thickness of about 15 to about 100 micrometers. The ceramic coating preferably has a total coating thickness of up to about 100 micrometers, and is deposited by a physical vapor deposition process to have a columnar and/or dense microstructure.