Method of producing barium-titanium-based oxide glass using containerless solidification process

Abstract

Disclosed is a method of producing a barium-titanium-based ferroelectric glass using a containerless solidification process, such as an electrostatic levitation process or a gas levitation process, which comprises the steps of levitating a sample 1 of a barium-titanium-based compound by a levitating force of compressed air, heating the sample up to a temperature greater than its melting point (1330° C.) by about 100° C. to allow the sample to be molten, and, after maintaining the molten state for a given time period (at least several second), quenching the sample from a given temperature range (1400 to 1000° C.) at a cooling rate of about 103 K/sec, so as to allow the sample to be solidified while inhibiting nucleation and mixing of impurities from a container. The present invention makes it possible to provide a glass exhibiting an unprecedented, extremely large permittivity.