Shoe sole component
AssigneeAsics Corporation
InventorsSadaki Mori, Katsuhiro Imazato, Kenichi Harano, Akiyuki Morikawa
Life of this patent
Estimating the term…
Abstract
There is provided a shoe sole component that has properties such as strength and cushioning property that are suppressed from being changed even under a wide temperature range from severe cold at −10° C. or lower to high temperature conditions exceeding 30° C. A shoe sole component includes a cross-linked foam of a resin composition, the resin composition containing a thermoplastic polyolefin resin, in which tan δ [−20° C. to 40° C.] at a frequency of 10 Hz measured according to JIS K 7244-4 is 0.01 to 0.5, and tan δ [−20° C.]/tan δ [40° C.] at a frequency of 10 Hz is 0.7 to 1.3.
Claims8
A shoe sole component comprising a cross-linked foam of a resin composition, the resin composition containing a first resin component of a thermoplastic polyolefin resin and a second resin component selected from the group consisting of a styrene resin and a thermoplastic polyolefin resin, wherein tan δ (−20° C. to 40° C.) at a frequency of 10 Hz measured according to JIS K 7244-4 is 0.01 to 0.5, and a ratio of tan δ (−20° C.)/tan δ (40° C.) at a frequency of 10 Hz is 0.7 to 1.3;
- wherein:
- the first resin component has the following properties:
- a ratio of tan δ (−20° C.)/tan δ (40° C.) at a frequency of 10 Hz measured according to JIS K 7244-4 of 0.5 to 1.5, a specific gravity measured according to JIS K 7311 of 0.85 to 0.95, a storage elastic modulus E′ (20° C.) at 20° C., and at a frequency of 10 Hz measured according to JIS K 7244-4 of 100 to less than 500 MPa, and a loss elastic modulus measured according to JIS K 7244-4 of not more than 40 MPa, and
- the second resin component has one of the following properties:
- a storage elastic modulus E′ (20° C.) at 20° C. and at a frequency of 10 Hz measured according to JIS K 7244-4 of 10 to less than 100 MPa and a loss elastic modulus measured according to JIS K 7244-4 of not more than 10 MPa;
- and
- a storage elastic modulus E′ (20° C.) at 20° C. and at a frequency of 10 Hz measured according to JIS K 7244-4 of 500 to 2000 MPa and a loss elastic modulus measured according to JIS K 7244-4 of not more than 50 MPa;
- and
- wherein the resin composition contains 60 to 95 parts by weight of the thermoplastic polyolefin resin of the first resin component in 100 parts by weight of the resin composition.
Dependencies are inferred from the claim text.