Salvage process for spring elements
AssigneeCaterpillar Inc.
InventorsSami El-Sayed, Howard D. Jenkel, Paul May
Life of this patent
Estimating the term…
Abstract
An improved method for salvaging a spring element with a degraded force constant for return to a work environment. The spring element is subjected to a high temperature and extended duration annealing treatment alone or in combination with other treatments. The resultant salvaged spring is characterized by a more durable force constant relative to the original spring when it was new.
Claims17
A method for recycling a spring element adapted for multiple load and recovery cycles during extended use, the spring element being characterized by a force constant at a first level when produced and having been subjected to a first number of load and recovery cycles in a first work environment such that the force constant has been reduced to a second level at a first average rate of degradation per cycle and thereafter recovered from said first work environment, the method comprising the steps of:
- (a) annealing said spring element at a level of about 500 to about 800 degrees Fahrenheit for about 8 to 12 hours such that said force constant is elevated from said second level to a third level between said first level and said second level;
- (b) placing said spring element in a second work environment;
- and
- (c) subjecting said spring element to a second number of load and recovery cycles such that said force constant is reduced at a second average rate of degradation per cycle, the second average rate of degradation per cycle being lower than the first average rate of degradation per cycle.
A method for recycling a spring element adapted for multiple load and recovery cycles during extended use, the method comprising the steps of:
- (a) providing a spring element characterized by a force constant at a first level;
- (b) subjecting said spring element to first number of load and recovery cycles in a first work environment such that said force constant is reduced to a second level at a first average rate of degradation per cycle;
- (c) recovering said spring element from said work environment;
- (d) annealing said spring element at a level of about 500 to about 800 degrees Fahrenheit for about 8 to 12 hours such that said force constant is elevated from said second level to a third level between said first level and said second level;
- (e) placing said spring element in a second work environment;
- and
- (f) subjecting said spring element to a second number of load and recovery cycles such that said force constant is reduced at a second average rate of degradation per cycle, the second average rate of degradation per cycle being lower than the first average rate of degradation per cycle.
Dependencies are inferred from the claim text.