Material used to combat thermal expansion related defects in high temperature casting processes
AssigneeIGC Technologies, LLC
InventorsJeffrey J. Cieplewski, Andrew Callan, Rebecca Roti
Life of this patent
Estimating the term…
Abstract
An additive to foundry sand molding and core aggregates is used to produce sand cores and molds comprising kyanite, spodumene, titanium dioxide, ilmenite and black iron oxide. The additive produces a sand-based foundry molding and core aggregate which resists the formation of some of the defects commonly associated with the production of castings produced by silica sand-based molding and core aggregates. In particular, the additive improves the quality of castings poured at temperatures higher than those of the pouring temperatures of molten iron, such as in steel castings, and in iron castings with “hot spots.”
Claims4
A material used to combat thermal expansion defects in silica sand foundry molds or cores at temperatures higher than those of the pouring temperatures of molten iron, said material comprising kyanite, spodumene, titanium dioxide, ilmenite and black iron oxide.
A method of making a metal casting from silica sand foundry molds or cores at temperatures higher than those of the pouring temperatures of molten iron comprising the steps of:
- preparing a mixture comprising at least about 80% by weight of silica sand, between about 0.5% to about 10% by weight of a binder, and at least about 7% by weight of a material used to combat thermal expansion defects, said material comprising kyanite, spodumene, titanium dioxide, ilmenite and black iron oxide;
- shaping said mixture to form the sand mold or core having a desired pattern therein;
- and
- pouring molten metal into said pattern, allowing the molten metal to cool and harden, and removing the mold or core to produce a metal casting.
Dependencies are inferred from the claim text.