Etching method for nitride semiconductor
AssigneeNational Chiao Tung University
InventorsWei-I Lee, Hsin-Hsiung Huang, Hung-Yu Zeng
Life of this patent
Estimating the term…
Abstract
The invention discloses etching method for the nitride semiconductor. Firstly dielectric layer is formed on gallium nitride. The line pattern or dot pattern is formed on the dielectric layer by using the exposure, development, and etching processes. The dielectric layer is used as the mask for the epitaxial lateral overgrowth of follow-up gallium nitride layer. The thick gallium nitride film is grown on the dielectric layer. Then the wet etching process is used to remove the dielectric layer, and the thick gallium nitride film on the dielectric layer is etched to form the specific shape as required.
Claims4
A method for etching a gallium nitride semiconductor having a hexagonal cone shape formed thereon by using a lateral etching process, comprising:
- providing a semiconductor substrate, forming a first gallium nitride layer on the semiconductor substrate, forming a dielectric layer discontinuously on a surface of the first gallium nitride layer, forming a second gallium nitride layer on the dielectric layer and the first nitride layer, wherein a thickness of the second gallium nitride layer being thicker than that of the first gallium nitride layer;
- first, using a lateral etching process to remove the dielectric layer;
- second, using the lateral etching process to remove the second gallium nitride layer on the dielectric layer to form as a hole;
- third, using the lateral etching process to remove the second gallium nitride layer for expanding the hole, so as to form a specific shape of the second gallium nitride layer;
- and
- removing the semiconductor substrate and the first gallium nitride layer, so that a hexagonal cone shape is formed on the second gallium nitride semiconductor.
Dependencies are inferred from the claim text.