High density dual helical gear
AssigneeKeystone Investment Corporation
InventorGary L. Anderson
Life of this patent
Estimating the term…
Abstract
The present invention relates to a low cost technique for manufacturing dual helical gears, such as herringbone gears, from powder metals. The dual helical gears made by this technique are of high density (greater than 92% of theoretical density) and offer superior strength. The present invention more specifically discloses a forged metal herringbone gear which is comprised of a body and a plurality of teeth wherein the metal has a density of greater than 92% of theoretical and wherein the grain in the teeth is one range higher on the ASTM E 112 grain size chart than the grain in the body of the gear.
Claims18
A high density forged dual helical gear including a body and a plurality of gear teeth produced by a method comprising the steps of:
- placing a heated sintered powder metal preform in a split mold cavity of a spilt mold die having a top die and a bottom die, wherein said top die has a top mold cavity and said bottom die has a bottom mold cavity, wherein said top mold cavity is a first helical gear shaped cavity, and said bottom mold cavity is a second helical gear shaped cavity, wherein at least one of said top die or bottom die is a rotating die member;
- and
- axially impacting the heated sintered powder metal preform with an upper punch and a lower punch, wherein at least one of said upper punch or said lower punch have teeth which mate with said first helical gear shape or said second helical gear shape respectively, and wherein whichever punch has teeth which mate with a helical gear shape is a rotating punch, wherein said heated sintered powder metal preform is axially impacted with sufficient force to densify said preform into the high density forged dual helical gear, wherein the high density forged dual helical gear has a density of greater than 92% of theoretical density, and wherein the grain size of the gear teeth is at least one range higher on the ASTM E 112 grain size chart than the grain in the body of the gear.
A high density forged internal dual helical gear including a body and a plurality of gear teeth produced by a method comprising the steps of:
- placing a heated sintered powder metal preform in a spilt mold die having a top die and a bottom die, wherein said top die has a top mold cavity and said bottom die has a bottom mold cavity, wherein said top mold cavity has a top core rod with a first helical gear profile, and said bottom mold cavity has a bottom core rod with a second helical gear profile, wherein at least one of said top core rod or bottom core rod is a rotating core rod;
- and
- axially impacting the heated sintered powder metal preform with an upper punch and a lower punch, wherein at least one of said upper punch or said lower punch have teeth which mate with said first helical gear profile or said second helical gear profile respectively, and wherein whichever punch has teeth which mate with a helical gear profile is a rotating punch, and further if one of said top core rod or said bottom core rod is a non-rotating core rod, the corresponding punch is a rotating punch with a mating helical gear profile, wherein said heated sintered powder metal preform is axially impacted with sufficient force to densify said preform into the high density forged internal dual helical gear, wherein the high density forged internal dual helical gear has a density of greater than 92% of theoretical density, and wherein the grain size of the gear teeth is at least one range higher on the ASTM E 112 grain size chart than the grain in the body of the gear.
A high density forged dual helical gear having a body, an external first helical gear profile having gear teeth, and an internal second helical gear profile having gear teeth, produced by a method comprising the steps of:
- placing a heated sintered powder metal preform in a split mold cavity of a spilt mold die having a top die and a bottom die, wherein said top die has a top mold cavity and said bottom die has a bottom mold cavity, wherein said top mold cavity is a first helical gear profile shaped cavity, and said bottom mold cavity has a bottom core rod with a second helical gear profile, wherein said top is a rotating die member;
- and
- axially impacting the heated sintered powder metal preform with an upper punch and a lower punch, wherein at least one of said upper punch or said lower punch have teeth which mate with said first helical gear profile or said second helical gear profile respectively, and wherein whichever punch has teeth which mate with a helical gear profile is a rotating punch, wherein said heated sintered powder metal preform is axially impacted with sufficient force to density said preform into the high density forged dual helical gear, wherein the high density forged dual helical gear has a density of greater than 92% of theoretical density, and wherein the grain size of the Rear teeth is at least one range higher on the ASTM E 112 grain size chart than the grain in the body of the gear.