US 7,842,335 B2 · Field repairable high temperature smooth wear coating

Abstract

A chemical composition and method for repairing a thermal barrier coating on a component designed for use in a hostile thermal environment, such as turbine, combustor and augmentor components of a gas turbine engine. The method repairs a thermal barrier coating on a component that has suffered localized damage to the thermal barrier coating. After cleaning the surface area of the component exposed by the localized spallation, a paste-like mixture of a ceramic composition comprising ceramic powders and nano-sized ceramic materials in a binder, further including an accelerant, is applied to the surface area of the component, and is optionally smoothed using mechanical means. The composition is then allowed to dry and cure to form a dried coating having polymeric characteristics. Upon subsequent heating, the dried coating reacts to produce a glassy ceramic repair coating. Due to the thixotropic properties of the coating composition upon application to a component, the repair method can be performed in-situ while the component remains installed in its operating environment.

Claims19

Dependent claims

A method for locally repairing a damaged thermal barrier coating on a component surface, the method comprising the steps of:

providing a ceramic coating composition comprising ceramic powders provided in two predetermined particle size ranges of less than 1 micron but greater than 30 nanometers and between about 45 microns to about 75 microns, respectively, at least one nano-sized ceramic material having a particle size of no greater than 30 nanometers, and a binder, the binder being chosen from the group consisting of ceramic precursor binders that thermally decompose to form a refractory material, an accelerant, and a solvent, the composition mixed to uniformly distribute the ceramic powders, nano-sized ceramic material, the binder, the accelerant, and the solvent;
applying the ceramic coating composition on a surface area of the component exposed by the localized damage;
mechanically smoothing the composition to form an uncured coating, the uncured coating composition characterized by the ability to flow when subjected to a mechanical stress and the ability to remain in place when the mechanical stress is removed;
and evaporating the solvent and curing the coating composition for a period sufficient to yield a dried coating that covers the surface area of the component, the dried coating comprising the ceramic powders and nano-sized ceramic material in a polymeric matrix.

1 more element

A method for repairing a region of localized spallation in a thermal barrier coating on a component installed in a gas turbine engine so as to expose a damaged surface area of the region of localized spallation defined at least in part by a bond coat overlying a component substrate surface and underlying the thermal barrier coating, the method comprising the steps of:

without removing the component from the gas turbine engine, dressing the surface area of the region of localized spallation so as to remove a predetermined region of thermal barrier coating without removing the bond coat from the substrate surface;
applying a composition to the surface area of the component exposed by the local spallation, the composition comprising a paste-like mixture of ceramic powders, a ceramic precursor binder, a nano-sized ceramic material suspended in the composition, and an accelerant, the ceramic powders provided in at least two predetermined particle size ranges of greater than 30 nanometers but less than 1 micron and comprising at least one of alumina, zirconia, hafnia, magnesia and silica, the binder being selected from the group consisting of silicone and phosphate-based compositions, the nano-sized ceramic material having a particle size of between 5 nanometers and 15 nanometers;
and evaporating the solvent to yield a dried coating that cures while drying to form a polymeric matrix that covers the surface area of the component.

Dependencies are inferred from the claim text.