Molecular sieve composition, a method of making and a process of using the same

A crystalline molecular sieve made by the steps of:

• (a) providing a mixture comprising at least one source of at least one tetravalent element (Y), at least one source of at least one alkali or alkali earth metal element, at least one directing-agent (R), water, and optionally at least one source of at least one trivalent element (X), said mixture having the following molar ratio:
• Y:X2=10 to infinity
• H2O:Y=1 to 10000
• OH−:Y=0.001 to 0.59
• M+:Y=0.001 to 2
• R:Y=0.001 to 2
• wherein M is an alkali metal and R is at least one N,N,N,N′N′N′-hexamethyl-1,5pentanediaminium salt(s), N,N,N,N′N′N′-hexamethyl-1,6-hexanediaminium salt(s), or any combination thereof, wherein said OH−:Y is calculated without trivalent element source correction;
• and
• (b) submitting the mixture at crystallization conditions to form a product comprising the desired crystalline molecular sieve, wherein the crystallization conditions comprise a temperature in the range of from 100° C. to 250° C., a stirring speed of ranging from at least 150 RPM to less than 5000 RPM, and a crystallization time from about 1 hour to 400 hours;
• and
• (c) recovering the crystalline molecular sieve.

A crystalline molecular sieve made by the method comprising the steps of:

• (a) providing a mixture comprising at least one source of at least one tetravalent element (Y), at least one source of at least one alkali or alkali earth metal element, at least one directing-agent (R), water, and optionally at least one source of at least one trivalent element (X), said mixture having the following molar ratio:
• Y:X2=10 to infinity
• H2O:Y=1 to 10000
• OH−:Y=0.74 to 2
• M+:Y=0.001 to 2
• R:Y=0.001 to 2
• wherein M is an alkali metal and R is at least one N,N,N,N′N′N′-hexamethyl-1,5-pentanediaminium salt(s), N,N,N,N′N′N′-hexamethyl-1,6-hexanediaminium salt(s), or any combination thereof, wherein said OH−:Y is calculated without trivalent element source correction;
• and
• (b) submitting the mixture at crystallization conditions to form a product comprising the desired crystalline molecular sieve, wherein the crystallization conditions comprise a temperature in the range of from 100° C. to 200° C., a stirring speed of ranging from at least 150 RPM to less than 5000 RPM, and a crystallization time from about 1 hour to 400 hours;
• and
• (c) recovering the crystalline molecular sieve.

A crystalline molecular sieve made by the method comprising the steps of:

• (a) providing a mixture comprising at least one source of at least one tetravalent element (Y), at least one source of at least one alkali or alkali earth metal element, at least one directing-agent (R), water, and optionally at least one source of at least one trivalent element (X), said mixture having the following molar ratio:
• Y:X2=10 to infinity
• H2O:Y=5 to 35
• OH−:Y=0.001 to 2
• M+:Y=0.001 to 2
• R:Y=0.001 to 2
• wherein M is an alkali metal and R is at least one N,N,N,N′N′N′-hexamethyl-1,5-pentanediaminium salt(s), N,N,N,N′N′N′-hexamethyl-1,6-hexanediaminium salt(s), or any combination thereof, wherein said OH−:Y is calculated with or without trivalent element source correction;
• and
• (b) submitting the mixture at crystallization conditions to form a product comprising the desired crystalline molecular sieve, wherein the crystallization conditions comprise a temperature in the range of from 100° C. to 200° C., a stirring speed of ranging from at least 150 RPM to less than 5000 RPM, and a crystallization time from about 1 hour to 400 hours;
• and
• (c) recovering the crystalline molecular sieve.

A crystalline molecular sieve made by the method comprising the steps of:

• (a) providing a mixture comprising at least one source of at least one tetravalent element (Y), at least one source of at least one alkali or alkali earth metal element, at least one directing-agent (R), water, at least one seed, and optionally at least one source of at least one trivalent element (X), said mixture having the following molar ratio:
• Y:X2=10 to infinity
• H2O:Y=1 to 10000
• OH−:Y=0.001 to 2
• M+:Y=0.001 to 2
• R:Y=0.001 to 2
• wherein M is an alkali metal and R is at least one N,N,N,N′N′N′-hexamethyl-1,5-pentanediaminium salt(s), N,N,N,N′N′N′-hexamethyl-1,6-hexanediaminium salt(s), or any combination thereof, wherein said OH−:Y is calculated with or without trivalent element source correction, wherein said seed has a concentration in said mixture ranging from about 0.01 to 10 wt% based on the weight of said tetravalent element oxide in said mixture;
• and
• (b) submitting the mixture at crystallization conditions to form a product comprising the desired crystalline molecular sieve, wherein the crystallization conditions comprise a temperature in the range of from 100° C. to 200° C., and a crystallization time from about 1 hour to 400 hours;
• and
• (c) recovering the crystalline molecular sieve.

A crystalline molecular sieve made by the method comprising the steps of:

• (a) providing a mixture comprising at least one source of at least one non- germanium tetravalent element (Y), at least one source of germanium (Ge), at least one directing-agent (R), water, and optionally at least one source of at least one trivalent element (X) and at least one source of at least one alkali or alkali earth metal element, said mixture having the following molar ratio:
• (Ge+Y):X2=10 to infinity
• H2O:Y=1 to 10000
• M+:Y=0 to 2
• R:Y=0.001 to 2
• wherein M is an alkali metal and R is at least one N,N,N,N′N′N′-hexamethyl-1,5-pentanediaminium salt(s), N,N,N,N′N′N′hexamethyl-1,6-hexanediaminium salt(s), or any combination thereof;
• and
• (b) submitting the mixture at crystallization conditions to form a product comprising the desired crystalline molecular sieve, wherein the crystallization conditions comprise a temperature in the range of from 100° C. to 200° C., and a crystallization time from about 1 hour to 400 hours;
• and
• (c) recovering the crystalline molecular sieve.