Aluminum hydroxide aggregated particles, process for producing the same, vessel used therefor, and process for producing aluminum hydroxide powder

A process for producing aluminum hydroxide aggregated particles of a filler for resins, comprising the steps of:

• (a) feeding a supersaturated aqueous sodium aluminate solution to a vessel,
• (b) adding aluminum hydroxide seeds to the supersaturated aqueous sodium aluminate solution to form a seed-added solution in the vessel,
• (c) stirring the seed-added solution in the vessel while continuously feeding an additional supersaturated aqueous sodium aluminate solution into the vessel to hydrolyze the supersaturated aqueous sodium aluminate solution to obtain aluminum hydroxide aggregated particles and an aqueous sodium aluminate solution, wherein the stirring is conducted with a mechanical stirrer having a stirring blade rotating at a peripheral velocity of not less than 0.1 m/s,
• (d) separating the aluminum hydroxide aggregated particles from the aqueous sodium aluminate solution, and
• (e) continuously discharging the aqueous sodium aluminate solution out of the vessel,
• wherein said vessel is a vessel for bringing a slurry composed an aqueous solution and aggregated particles to a substantially complete mixing state, having a hollow space defined by a surrounding wall and a bottom part, wherein the vessel has:
• a supply port at a lower portion of the wall,
• two or more baffle plates mounted on an inner surface of the wall so that the baffle plates protrude toward the hollow space and extend in vertical direction along the inner surface of the wall from immediately above the bottom part to a prescribed height from the bottom part, and
• a stirring blade located within the hollow space and within a space below the prescribed height of the baffle plates;
• and
• straightening vanes;
• wherein the baffle plates improve stirring efficiency, such that at the time of stirring, an ascending current is formed along the inner surface of the wall of vessel, whereby a slurry in a concentrating region specified by the height of baffle plates can be brought to a substantially complete mixing state, and
• wherein the straightening vanes are provided on the inner surface of the wall, so that the straightening vanes protrude toward the hollow space and are located on the wall above the baffle plates, and the straightening vanes promote separation of an aqueous solution and aggregated particles from each other in the concentrating region and improve the clarity of the aqueous solution.