Foamed-wall container having a silvery appearance
AssigneePlastic Technologies, Inc.
InventorsFrank E. Semersky, William D. Voyles, Eugene M. Sadzewicz
Life of this patent
Estimating the term…
Abstract
A container comprises a micro cellular foamed polymer, and a non-reactive gas contained within the micro cellular foam cells, wherein the container has a silvery appearance. The process for making the container comprises injection molding a polymer preform having a non-reactive gas entrapped within the walls thereof, cooling the preform to a temperature below the polymer softening temperature, reheating the preform to a temperature above the polymer softening temperature, and blow molding the preform, to prepare a container comprising a micro cellular foamed polymer having a non-reactive gas contained within the micro cellular foam cells.
Claims17
A blow molded container, comprising:
- a micro cellular foamed polymer formed without a chemical blowing agent suitable for blow molding having micro cellular foam cells, comprising polyethylene terephthalate;
- and
- a non-reactive gas contained within the micro cellular foam cells comprising one or more of carbon dioxide, nitrogen, or argon, wherein the color of the blow molded container is Pantone Color Formula Guide number 420, 421, 422, 423, 424, 425, 877, 8001, 8400, or 8420 without the use of a colorant.
A blow molded container, comprising:
- a micro cellular foamed polyethylene terephthalate formed without a chemical blowing agent suitable for blow molding having micro cellular foam cells;
- and
- a non-reactive gas comprising nitrogen contained within the micro cellular foam cells, wherein the color of the blow molded container is Pantone Color Formula Guide number 877 without the use of a colorant.
A process for preparing a container, comprising the steps of:
- injection molding a polymer preform having a non-reactive gas entrapped within the walls thereof;
- cooling the preform to a temperature below the polymer softening temperature;
- reheating the preform to a temperature greater than the polymer softening temperature;
- and
- blow molding the preform, to prepare a plastic container having a silvery appearance without the use of a colorant, consisting essentially of a micro cellular foamed polymer having the non-reactive gas contained within the micro cellular foam cells;
- and
- the silvery appearance without the use of a colorant is as though the plastic container were made of metal having a silver color.
A process for preparing a container, comprising the steps of:
- injection molding a preform comprising a polymer comprising one or more of a polyester, polypropylene, acrylonitrile acid ester polymer, vinyl chloride polymer, polyolefin, polyamide, or a derivative or copolymer thereof, the preform having a non-reactive gas comprising one or more of carbon dioxide, nitrogen, or argon entrapped within the walls thereof;
- cooling the preform to a temperature below about 70 degrees Centigrade;
- reheating the preform to a temperature above about 70 degrees Centigrade;
- and
- blow molding the preform, to prepare a plastic container having a silvery appearance without the use of a colorant comprising a micro cellular foamed polymer having the non-reactive gas contained within the micro cellular foam cells;
- and
- the silvery appearance without the use of a colorant is as though the plastic container were made of a metal having a silver color.
A process for preparing a micro cellular preform suitable for blow molding a plastic container comprising the steps of:
- injection molding a micro cellular polymer preform having a non-reactive gas entrapped within the walls thereof;
- cooling the preform to a temperature below the polymer softening temperature;
- and
- reheating the preform to a temperature above the glass transition temperature of the polymer and below the temperature at which the increasing pressure of the micro cellular gas bubbles exceeds that of the ability of the polymer preform material properties to resist and the micro cellular bubbles expand to result in a distorted preform, wherein the micro cellular preform comprises a hollow body having a silvery appearance without the use of a colorant and the silvery appearance is as though the preform of the plastic container were made of metal having a silver color.
Dependencies are inferred from the claim text.