# US 7,745,513 B2 · Fluoropolymer compositions and inorganic nanometric particles

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 7,745,513 B2
- Document ID: US7745513B2
- Status: Granted
- Kind: B2
- Application number: 10/453,927
- Filed: 2003-06-04
- Published: 2003-12-11
- Granted: 2010-06-29
- Earliest claimed: 2002-06-04
- Assignees: Solvay Solexis S.p.A.
- Inventors: Julio A. Abusleme; Aldo Sanguineti; Claudia Manzoni
- Web page: https://patentgrep.com/patent/US7745513B2

## CPC

- C08K 3/34: Silicon-containing compounds
- C08K 7/00: Use of ingredients characterised by shape
- Y10T 428/2982: Particulate matter [e.g., sphere, flake, etc.]
- Y10T 428/3154: Of fluorinated addition polymer from unsaturated monomers
- C08K: Use of inorganic or non-macromolecular organic substances as compounding ingredients (paints, inks, varnishes, dyes, polishes, adhesives C09)
- Y10T: TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION

## Abstract

A polymeric composition comprising: a) from 90 to 99.9% by weight of a continuous fluoropolymer matrix; and homogeneously dispersed b) from 0.1 to 10% by weight of lamellar inorganic particles having at least one dimension lower than 100 nm having improved elastic modulus and “storage modulus” G′ at high temperatures.

## Claims

### Claim 1

A process for manufacturing a polymeric composition comprising:
a) from 90 to 99.9% by weight of a fluoropolymer; and homogeneously dispersed
b) from 0.1 to 10% by weight of non-modified lamellar inorganic particles having a thickness lower than 100 nm,
said process comprising the steps of:
1) preparing an aqueous fluoropolymer latex having a concentration between 5 and 60% by weight of fluoropolymer;
2) preparing an aqueous dispersion of lamellar inorganic particles having a thickness lower than 100 nm, and the other two dimensions lower than 10,000 nm by mixing an inorganic component having a layered lamellar morphology with water until obtaining a concentration comprised between 0.1 and 10% by weight under stirring at a temperature in the range 20° C.-300° C.
3) mixing, under stirring, the latex obtained in step 1) with the aqueous dispersion obtained in step 2) wherein the ratio by weight of the fluoropolymer to the lamellar inorganic component is in a range of 1:1-1000:1;
4) effecting precipitation of a solid phase from the aqueous mixture obtained in step 3) by cooling at a temperature lower than 0° C. to −20° C. or by increasing the ionic force or by pH variations; and
5) separating and drying at temperatures from 50° C. to 250° C. the solid phase obtained in step 4) to obtain the polymeric composition.

### Claim 2 (depends on 1)

The process according to claim 1, wherein the fluoropolymer of the latex in the form of particles has dimensions between 20 and 300 nm.

### Claim 3 (depends on 1)

The process according to claim 1, wherein the fluoropolymer latex in the form of particles has dimensions between 50 and 150 nm.

### Claim 4 (depends on 1)

The process according to claim 1, wherein the lamellar inorganic particles have a thickness lower than 50 nm.

### Claim 5 (depends on 1)

The process according to claim 1, wherein the other two dimensions of the lamellar inorganic particles are lower than 2000 nm.

### Claim 6 (depends on 1)

The process of claim 1, wherein the inorganic component having a layered lamellar morphology is mixed with water until obtaining a concentration between 0.5 and 2%.

### Claim 7 (depends on 1)

The process of claim 1, wherein mixing the inorganic component having a layered lamellar morphology with water under stirring is performed at a temperature in the range 50° C.-100° C.

### Claim 8 (depends on 1)

The process of claim 1, wherein the stirring is at least one of a strong mechanical stirring and an ultrasound treatment.

### Claim 9 (depends on 1)

The process of claim 1, wherein the lamellar inorganic particles have a thickness lower than 10 nm.

### Claim 10 (depends on 1)

The process according to claim 1, wherein the other two dimensions of the lamellar inorganic particles are lower than 500 nm.

### Claim 11 (depends on 1)

The process of claim 1, wherein the fluoropolymer a) is a semicrystalline fluoropolymer having a second melting temperature lower than 310° C.

### Claim 12 (depends on 1)

The process of claim 1, wherein the fluoropolymer a) is selected from the group consisting of:
chlorotrifluoroethylene homopolymer (POTFE) and semicrystalline thermoplastic copolymers of chlorotrifluoroethylene (CTFE) in amounts in the range 0.1-5% by moles of fluorinated monomers or acrylic monomers and semicrystalline thermoplastic copolymers of ethylene (E) with CTFE and/or TFE.