Process for preparing dispersed ingredient having metal-oxygen bonds
AssigneeNippon Soda Co., Ltd.
InventorsMotoyuki Toki, Akiji Higuchi, Nobuo Kimura, Yoshitaka Fujita
Life of this patent
Estimating the term…
Abstract
A dispersed ingredient having metal-oxygen bonds which is obtained by hydrolyzing a metal alkoxide in an organic solvent in the absence of an acid, a base, and/or a dispersion stabilizer, either with 0.5 to less than 1 mol of water per mol of the metal alkoxide or at −20° C. or lower with 1.0 to less than 2.0 mol of water per mol of the metal alkoxide. In the organic solvent, the dispersed ingredient is stably dispersed without aggregating. Use of the dispersed ingredient enables a thin metal oxide film and a homogeneous organic/inorganic composite to be produced at a temperature as low as 200° C. or below.
Claims6
A process for preparing a dispersed ingredient having metal-oxygen bonds that is stably dispersed in an organic solvent without aggregating, the dispersed ingredient having a transmittance of 80-100%, the transmittance being measured under conditions in which a concentration of the dispersed ingredient is 0.5% by weight in terms of oxide, an optical path length of a quartz cell is 1 cm, a control sample is the organic solvent, and a light wavelength is 550 nm, the process comprising:
- hydrolyzing a metal alkoxide with water in the organic solvent without the addition of acids, bases and dispersion stabilizers;
- wherein
- the metal alkoxide is hydrolyzed with 1.0 to less than 2.0 mol of water per mol of the metal alkoxide at a temperature from −50° C. to −100° C.