Wire for high-speed electrical discharge machining
AssigneeThermocompact
InventorMichel Ly
Life of this patent
Estimating the term…
Abstract
The invention concerns an electrode wire comprising an unalloyed copper core coated with a diffused zinc alloy coating layer, whereof the thickness is more than 10% of the wire diameter. The coating layer is optionally plated with a thin zinc, copper, nickel, silver or gold surface contact film. Such a wire achieves higher electrical discharge machining speed.
Claims6
A spark erosion machining electrode wire comprising a metal core coated with a coating layer of diffused zinc alloy, wherein:
- the core is of unalloyed copper,
- the coating layer is of diffused copper and zinc alloy,
- the thickness of the coating layer of copper and zinc alloy is greater than about 10% of the diameter of the electrode wire, and
- the overall electrical conductivity of the electrode wire is from about 65% IACS to about 75% IACS.
A method of producing a spark erosion electrode wire, said wire comprising a metal core coated with a coating layer of diffused zinc alloy, wherein:
- the core is of unalloyed copper,
- the coating layer is of diffused cooper and zinc alloy, and
- the thickness of the coating layer of copper and zinc alloy is greater than about 10% of the diameter of the electrode wire, said method comprising the following steps:
- a. providing an unalloyed copper core wire of diameter greater than the diameter of the spark erosion electrode wire to be produced,
- b. coating the core wire with pure zinc to form a coated core wire,
- c. subjecting the coated core wire to diffusion heat treatment to form a coating layer,
- d. drawing the coated core wire to the final diameter, the coating layer then having a thickness greater than 10% of the final diameter of the spark erosion electrode wire, wherein the overall electrical conductivity of the spark erosion electrode wire is from about 65% IACS to about 75% IACS.
A method for machining a part by spark erosion in a machine employing an electrical generator to produce the sparking electrical enemy, the method comprising generating sparks between an electrode wire and the part, producing relative movement of the electrode wire and the part transversely to the longitudinal direction of the electrode wire, and eroding the part, wherein:
- the generator is set to produce the maximum sparking energy compatible with the machining capacity of the electrode wire without breaking the electrode wire, thereby increasing the machining rate, and the electrode wire is a spark erosion machining electrode wire comprising a metal core coated with a coating layer of diffused zinc alloy, wherein:
- the core is of unalloyed cooper,
- the coating layer is of diffused copper and zinc alloy, and
- the thickness of the coating layer of copper and zinc alloy is greater than about 10% of the diameter of the electrode wire, wherein the overall electrical conductivity of the electrode wire is from about 65% IACS to about 75% IACS.
Dependencies are inferred from the claim text.