Method for preparation of steel material
AssigneeHonda Giken Kogyo Kabushiki Kaisha
InventorMitsuo Kuwabara
Life of this patent
Estimating the term…
Abstract
A raw steel is coated with or surrounded by a boron compound (step S1). A coating film of h-BN is formed on the surface of the raw steel. Then, the raw steel is nitrided by a nitriding gas while being heated (step S2). B from the boron compound and N from the nitriding gas are diffused into the raw steel, turning the raw steel into a steel material containing B and N. Most of B and N are present as an Fe (B, N) solid solution or an Fe (C, B, N) solid solution in the structure of the steel material. The raw steel is heated and nitrided under conditions such that B and N are contained ranging from 7 to 30 ppm by weight and ranging from 10 to 70 ppm by weight, respectively.
Claims5
A method of manufacturing a steel material, comprising the steps of:
- covering or surrounding a raw steel with a boron compound comprising hexagonal BN or B4C;
- and
- nitriding said raw steel with a nitriding gas while heating said raw steel in a temperature range from 1100 to 1750 K thereby causing B and N to diffuse into the raw steel so that said steel material comprises B ranging from 7 to 30 ppm by weight and N ranging from 10 to 70 ppm by weight,
- and wherein B diffuses into the raw steel by a distance in excess of 0.3 mm from a surface of the raw steel.
Dependencies are inferred from the claim text.