Ceramic nanostructures and methods of fabrication
AssigneeBabcock & Wilcox Technical Services Y-12, LLC
InventorsEdward B. Ripley, Roland D. Seals, Jonathan S. Morrell
Life of this patent
Estimating the term…
Abstract
Structures and methods for the fabrication of ceramic nanostructures. Structures include metal particles, preferably comprising copper, disposed on a ceramic substrate. The structures are heated, preferably in the presence of microwaves, to a temperature that softens the metal particles and preferably forms a pool of molten ceramic under the softened metal particle. A nano-generator is created wherein ceramic material diffuses through the molten particle and forms ceramic nanostructures on a polar site of the metal particle. The nanostructures may comprise silica, alumina, titania, or compounds or mixtures thereof.
Claims19
A plurality of generally columnar nanoparticles, each generally columnar nanoparticle and having a longitudinal section and each longitudinal section of each generally columnar nanoparticle being interconnected to the longitudinal section of at least one other of the plurality of generally columnar nanoparticles and each columnar nanoparticle having an end with a tapered ridged cap and the ends of the columnar nanoparticles being interconnected in a substantially dendritic pattern.
A nanostructure derived from an interface between a softened metal catalyst particle and a nano-ceramic substrate, the nanostructure comprising a plurality of generally columnar nanoparticles wherein the generally columnar nanoparticles each have a longitudinal axis and the longitudinal axes of the generally columnar nanoparticles are substantially parallel and the nanostructure has a curtain-like pattern on a radial fracture face.
A process for fabricating a nanostructure, the process comprising the steps:
- (a) disposing a metal catalyst particle having a boiling point on a substrate comprising a nano-ceramic material that dissolves in the metal catalyst particle at a temperature less than the boiling point of the metal catalyst particle, wherein a substrate interface is formed where the metal catalyst particle rests on the substrate;
- (b) heating the metal catalyst particle and the substrate to a temperature between (1) a temperature at which at least a portion of the nano-ceramic material dissolves into the metal catalyst particle at the substrate interface and (2) the boiling point of the metal catalyst particle;
- (c) pumping at least a portion of the nano-ceramic material from the substrate into the metal catalyst particle until a nanostructure comprising the nano-ceramic material forms on a polar site of the metal catalyst particle, the polar site being substantially opposed to the substrate interface;
- and
- (d) cooling the metal catalyst particle containing the pumped nano-ceramic material and the nanostructure to an ambient temperature.