# US 7,612,119 B2 · Expandable vinylaromatic polymers and process for their preparation

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 7,612,119 B2
- Document ID: US7612119B2
- Status: Granted
- Kind: B2
- Application number: 10/551,524
- Filed: 2004-03-11
- Published: 2006-12-07
- Granted: 2009-11-03
- Earliest claimed: 2003-03-31
- Assignees: Polimeri Europa S.p.A.
- Inventors: Antonio Ponticiello; Alessandra Simonelli; Loris Zamperlin
- Web page: https://patentgrep.com/patent/US7612119B2

## CPC

- C08J 9/16: Making expandable particles
- C08J 9/0066: {Use of inorganic compounding ingredients}
- C08J 2325/04: Homopolymers or copolymers of styrene
- C08J: WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H (working, e.g. shaping, of plastics B29)

## Abstract

Expandable vinylaromatic polymers which comprise: a) a matrix obtained by polymerizing 50-100% by weight of one or more vinylaromatic monomers and 0-50% by weight of a copolymerizable monomer; b) 1-10% by weight, calculated with respect to the polymer (a) of an expanding agent englobed in the polymeric matrix; c) 0.01-20% by weight, calculated with respect to the polymer (a) of carbon black distributed in the polymeric matrix having an average diameter ranging from 30 to 2000 nm, a surface area ranging from 5 to 40 m2/g, a sulfur content ranging from 0.1 to 2000 ppm and an ash content ranging from 0.001 to 1%.

## Claims

### Claim 1

An expandable vinylaromatic polymer, comprising:
a) a polymeric matrix obtained by polymerizing 50-100% by weight of one or more vinylaromatic monomers and 0-50% by weight of a copolymerizable monomer;
b) 1-10% by weight, calculated with respect to the polymer (a), of an expanding agent embedded in the polymeric matrix;
c) 0.01-20% by weight, calculated with respect to the polymer (a), of carbon black homogeneously distributed in the polymeric matrix and having an average diameter ranging from 30 to 2000 nm, a surface area ranging from 5 to 40 m2/g, a sulfur content ranging from 0.1 to 2000 ppm and an ash content ranging from 0.001 to 1%.

### Claim 2 (depends on 1)

The polymers according to claim 1, wherein the carbon black has a weight loss with heat ranging from 0.001 to 1%, an iodine number ranging from 0.00 1 to 20 g/kg and an absorption value of dibutylphthalate ranging from 5 to 100 ml/(100 g).

### Claim 3 (depends on 1)

The polymers according to claim 1, wherein the vinylaromatic monomer is selected from the group consisting of monomers the following general formula:
wherein R is a hydrogen or a methyl group, n is zero or an integer ranging from 1 to 5 and Y is a halogen, or an alkyl or alkoxyl radical having from 1 to 4 carbon atoms.

### Claim 4 (depends on 3)

The polymers according to claim 3, wherein the vinylaromatic monomer having general formula (I) is used in a mixture, of up to 50% by weight, with at least one other copolymerizable monomer selected from the group consisting of (meth)acrylic acid, C1-C4 alkyl esters of (meth)acrylic acid, amides of (meth) acrylic acid, nitriles of (meth)acrylic acid, butadiene, ethylene, divinylbenzene, and maleic anhydride.

### Claim 5 (depends on 4)

The polymers according to claim 4, wherein the copolymerizable monomer is acrylonitrile and methylmethacrylate.

### Claim 6 (depends on 1)

The polymers according to claim 1, wherein the carbon black has an average diameter ranging from 100 to 1000 nm, a surface area ranging from 8 to 20 m2/g, (measured according to ASTM D-6556), a sulfur content ranging from 1 to 500 ppm, an ash residue ranging from 0.01 to 0.3% (measured according to ASTM D-1506), a weight loss with heat (measured according to ASTM D-1509) ranging from 0.01 to 0.5%, an absorption value of dibutylphthalate (measured according to ASTM D-2414) of 20-80 ml/(100 g) and an iodine number (measured according to ASTM D-1510) ranging from 0.1 to 10 g/kg.

### Claim 7 (depends on 1)

The polymers according to claim 1, wherein the carbon black is used in a quantity ranging from 0.1 to 5% by weight, with respect to the polymer.

### Claim 8 (depends on 1)

An expandable article, comprising:
an expandable vinylaromatic polymer according to claim 1, having a density ranging from 5 to 50 g/l and a thermal conductivity ranging from 25 to 50 mW/mK, at least 10% lower than that of equivalent-expanded materials without carbon black.

### Claim 9

A process for the preparation of an expandable vinylaromatic polymer, comprising:
polymerizing in aqueous suspension one or more vinylaromatic monomers, optionally together with at least one polymerizable comonomer in a quantity of up to 50% by weight, in the presence of a carbon black having an average diameter ranging from 30 to 2000 nm, a surface area ranging from 5 to 40 m2/g, a sulfur content ranging from 0.1 to 2000 ppm and an ash content ranging from 0.001 to 1%, and in the presence of a peroxide radicalic initiator, optionally containing at least one aromatic ring, and at least one expansion agent added before, during or at the end of the polymerization.

### Claim 10 (depends on 9)

The process according to claim 9, wherein the carbon black has weight loss with heat ranging from 0.001 to 1%, an iodine number ranging from 0.001 to 20 g/kg and an absorption value of dibutylphthalate ranging from 5 to 100 ml/(100 g).

### Claim 11 (depends on 9)

The process according to claim 9, wherein the polymerization is carried out in the presence of an organic suspending agent, an inorganic suspending agent or both.

### Claim 12 (depends on 11)

The process according to claim 11, wherein the inorganic suspending agent is coadjuvated by an anionic surface-active agent or sodium metadisulfite.

### Claim 13 (depends on 9)

The process according to claim 9, wherein the polymerization in suspension is effected through a solution of vinylaromatic polymer in the monomer, or mixture of monomers, in which the concentration of polymer ranges from 1 to 30% by weight.

### Claim 14 (depends on 9)

The process according to claim 9, wherein, at the end of the polymerizations beads of polymer are obtained in a substantially spherical form, with an average diameter ranging from 0.2 to 2 mm inside which the carbon black filler is homogeneously dispersed.

### Claim 15 (depends on 14)

The process according to claim 14, wherein the polymer beads obtained at the end of the polymerization are washed with a non-ionic surface-active agent.

### Claim 16 (depends on 9)

The process according to claim 9, wherein during the polymerization, at least one polymerization flame-retardant agent is added in a quantity ranging from 0.1 to 8% by weight, with respect to the weight of the resulting polymer.

### Claim 17 (depends on 9)

The process according to claim 9, wherein the at least one expansion agent is added during the polymerization phase and is selected from the group consisting of aliphatic hydrocarbons comprising 3 to 6 carbon atoms, cycloaliphatic hydrocarbons comprising from 3 to 6 carbon atoms, halogenated derivates of aliphatic hydrocarbons comprising from 1 to 3 carbon atoms, carbon dioxide and water.

### Claim 18

A process for preparing, in mass and continuously, an expandable vinylaromatic polymer which comprises, in series:
i. feeding a vinylaromatic polymer to an extruder, together with a carbon black filler, having an average diameter ranging from 30 to 2000 nm, a surface area ranging from 5 to 40 m2/g, a sulfur content ranging from 0.1 to 2000 ppm and an ash residue ranging from 0.001 to 1%;
ii. heating the vinylaromatic polymer to a temperature higher than the relative melting point, to obtain a molten polymer;
iii. injecting an expanding agent and optionally an additive, into the molten polymer before extrusion through a die; and
iv. forming expandable beads, through a die, in a substantially spherical form with an average diameter ranging from 0.2 to 2 mm.

### Claim 19 (depends on 18)

The process according to claim 18, wherein the carbon black filler has by has a weight loss with heat ranging from 0.001 to 1%, an iodine number ranging from 0.001 to 20 g/kg and an absorption value of dibutylphthalate ranging from 5 to 100 ml/(100 g).

### Claim 20 (depends on 18)

The process according to claim 18, further comprising:
a) pretreating the expandable beads by coating with a liquid antistatic agents, to obtain pre-treated beads;
b) applying a coating to the pre-treated beads, said coating comprising (i) a mixture of mono-, di- and tri-esters of glycerin with fatty acid, (ii) a metallic stearate or (iii) a combination of (i) and (ii);
wherein the liquid antistatic agent is selected from the group consisting of amines, tertiary ethoxylated alkylamines and ethylene oxide propylene oxide copolymers.

### Claim 21 (depends on 20)

The process according to claim 20, wherein the carbon black filler is also added to the coating together with the mixture of esters.

### Claim 22 (depends on 18)

The process according to claim 18, wherein a flame retardant is added in step iii.

### Claim 23 (depends on 20)

The process according to claim 20, wherein the metallic stearate is zinc stearate or magnesium stearate.