Translucent lutetium oxide sinter, and method for manufacturing same
AssigneeKonoshima Chemical Co., Ltd.
InventorsShunsuke Hosokawa, Hideki Yagi, Takagimi Yanagitani
Life of this patent
Estimating the term…
Abstract
The present invention provides a lutetium oxide sinter to which yttrium is added in an amount of 100 mass ppm to 7000 mass ppm, whose average particle size is from 0.7 to 20 μm, and with which there is no precipitation of a hetero phase containing yttrium at the grain boundary.
Claims5
A translucent sinter consisting essentially of lutetium oxide and having a yttrium content of at least 100 mass ppm and not more than 0.7 mass %, and the linear optical transmissivity at a thickness of 1 mm over a wavelength region from 500 nm to 6.5 μm is at least 80%.
A method for manufacturing a translucent sinter consisting essentially of lutetium oxide, being characterized in that a lutetium oxide powder with a BET (specific surface area) value of at least 2.0 m2/g and not more than 15.0 m2/g, a mass percentage of aggregated particles of 5 μm or larger of not more than 10%, and a purity of at least 99.9% is used to produce a molded article with a theoretical density ratio of at least 58% and a yttrium content of at least 100 mass ppm and not more than 0.7 mass %, and
- this molded article is sintered for at least 0.5 hour in hydrogen, a rare gas, or a mixed atmosphere of these, or in a vacuum, at a temperature of at least 1450° C. and not higher than 1750° C. to create a lutetium oxide sinter.