Method for the aesthetic surface treatment of a monolithic concrete floor and product of the method
AssigneeTerr-Con Decorative Concrete Floors, Inc.
InventorsRonald F. Palermo, Christopher F. Leva, Patrick T. Leva
Life of this patent
Estimating the term…
Abstract
This invention relates generally to a method for forming a concrete floor as a monolithic unit, wherein a wet concrete mix is deposited and worked to achieve a generally uniform flatness of concrete and adding to the top layer thereof a decorative aggregate material. Subsequently, the surface of the concrete is worked, allowed to partially cure and then ground and polished to substantially remove surface irregularities and reveal the decorative aggregate. The floor surface may then be coated with a sealant to achieve a terrazzo-like appearance.
Claims17
A method for forming an integrated ornamental surface on a monolithic concrete floor concurrent with the pouring and finishing of the concrete floor, comprising the following steps in order:
- preparing and forming the region upon which the monolithic concrete floor is to be poured;
- contiguously pouring concrete throughout the formed region to form a monolithic layer;
- floating the concrete to effectively densify the monolithic concrete layer;
- allowing the concrete layer to cure to a semi-stiff state;
- finishing the exposed upper surface of the concrete layer to produce a generally planar surface;
- disbursing a quantity of a decorative aggregate over only the surface of the semi-stiff concrete layer, wherein said decorative aggregate has a particulate size of at least 6 mm and no more than 50 mm;
- integrating the aggregate into the upper surface of the semi-stiff concrete;
- partially curing the concrete with the integrated aggregate;
- grinding the upper surface of the partially cured concrete with the integrated aggregate therein, including partially removing some of both the partially cured concrete and the integrated aggregate material at least until the aggregate is exposed uniformly over the top of the concrete, wherein said grinding step further comprises the steps of:
- a rough first pass using a rotary head concrete grinding machine having a cutting head of diamonds;
- a second pass using a finer grit on a disc comprised of silicon carbide and a bonding material;
- and
- a polishing pass with a rotary head polishing machine using between about a 200 grit to a 1600 grit diamond pad;
- fully curing the concrete with the integrated aggregate;
- and
- polishing the upper surface with the integrated aggregate to provide a generally planar and smooth surface on the monolithic concrete floor.
A method for forming an integrated ornamental surface on a monolithic concrete floor concurrent with the pouring and finishing of the concrete floor, comprising:
- preparing and forming a region upon which the monolithic concrete floor is to be poured;
- contiguously pouring concrete throughout the formed region to form a monolithic layer;
- screeding the exposed upper surface of the concrete layer to produce a generally planar surface;
- disbursing a quantity of a decorative aggregate over only the surface of the concrete layer, wherein said decorative aggregate has a particulate size of no more than 50 mm;
- integrating the aggregate into the upper surface of the concrete layer;
- partially curing the concrete with the integrated aggregate;
- grinding the upper surface of the partially cured concrete with the integrated aggregate therein to remove a layer of generally uniform thickness from the upper surface, including a rough first pass using a rotary head concrete grinding machine wherein said rough first pass uses a rotary cutting head of diamonds and a second pass using a finer grit on a disc comprised of silicon carbide and a bonding material, thereby removing some of both the partially cured concrete and the integrated aggregate material at least until the aggregate is exposed uniformly over, yet coplanar with, a top surface of the concrete;
- fully curing the concrete with the integrated aggregate;
- and
- polishing the upper surface with the integrated aggregate to provide a generally planar and smooth surface on the monolithic concrete floor.
A method for forming an integrated ornamental surface on a monolithic concrete floor concurrent with the pouring and finishing of the concrete floor, consisting essentially of:
- preparing and forming the region upon which the monolithic concrete floor is to be poured;
- contiguously pouring concrete throughout the formed region;
- floating the concrete to effectively densify the concrete;
- allowing the concrete to cure to a semi-stiff state;
- finishing the exposed upper surface of the concrete to produce a generally planar surface;
- disbursing a quantity of a decorative aggregate over only the surface of the semi-stiff concrete, wherein said decorative aggregate has a particulate size of at least 6 mm and no more than 50 mm;
- integrating the aggregate into the upper surface of the semi-stiff concrete;
- partially curing the concrete with the integrated aggregate;
- using a series of successively finer abrasives, grinding the upper surface of the partially cured concrete with the integrated aggregate therein, including removing a generally uniform layer including some of both the partially cured concrete and the integrated aggregate material at least until the remaining aggregate is exposed uniformly over the top of the concrete, wherein said grinding step further comprises
- a rough first pass using a rotary head concrete grinding machine having a cutting head of diamonds;
- a second pass using a finer grit on a disc comprised of silicon carbide and a bonding material;
- and
- a polishing pass with a rotary head polishing machine using between about a 200 grit to a 1600 grit diamond pads
- fully curing the concrete with the integrated aggregate;
- and
- polishing the upper surface with the integrated aggregate to provide a generally planar, smooth surface with exposed aggregate, on the monolithic concrete floor.
Dependencies are inferred from the claim text.