US 7,575,653 B2Granted
Melt-flowable materials and method of sealing surfaces
Assignee3M Innovative Properties Company
InventorsMichael A. Johnson, Clayton A. George, Peggy S. Willett, Scott R. Meyer
Life of this patent
Estimating the term…
Abstract
The invention provides a method for imparting topographical or protective features to a substrate by contacting a sheet material comprising a thermosettable layer with a substrate and heating the sheet material to an elevated temperature.
Claims28
A method for modifying a surface of a substrate comprising the steps of:
- (a) placing on said surface an article comprising (i) a melt-flowable composition and (ii) a dimensionally stable film for controlling the melt-flow behavior of said melt-flowable composition, such that said melt-flowable composition contacts said surface, said film being disposed above said melt-flowable composition and comprising a substantially smooth, paint-receptive upper surface comprising a thermosetting epoxy-polyester blend;
- (b) heating said article to cause said melt-flowable composition to flow and substantially cover a desired area of said surface to adhere said article to said surface, said dimensionally stable film controlling the melt-flow behavior of said melt-flowable composition to substantially confine said melt-flowable composition to said desired area of said surface;
- and
- (c) allowing said article to cool while substantially retaining said substantially smooth surface topography of said film.
1 more element
A method for modifying a surface forming part of a vehicle body comprising the steps of:
- (a) placing on said surface forming part an article comprising (i) a melt-flowable composition comprising a semi-crystalline, thermosetting epoxy-polyester blend and (ii) a dimensionally stable film for controlling the melt-flow behavior of said melt-flowable composition, such that said melt-flowable composition contacts said surface forming part, said film comprising an oriented polyester film having a substantially smooth surface topography;
- (b) heating said article to cause said melt-flowable composition to flow and substantially cover a desired area of said surface forming part to adhere said article to said surface forming part, said dimensionally stable film exhibiting a downweb and crossweb shrinkage of less than about 5% and controlling the melt-flow behavior of said melt-flowable composition to substantially confine said melt-flowable composition to said desired area of said surface forming part;
- and
- (c) allowing said article to cool while substantially retaining said substantially smooth surface topography of said film.
1 more element
A method for modifying a surface of a step joint in a vehicle body comprising the steps of:
- (a) placing a sheet material on the surface of the step joint, said sheet material comprising (i) a lower melt-flowable layer comprising a melt-flowable composition, the melt-flowable layer having a thickness in the range of at least about 0.05 mm up to about 25 mm, and (ii) a dimensionally stable film for controlling the melt-flow behavior of said melt-flowable composition, said film having a surface topography and being sufficiently dimensionally stable so as not to melt and flow or exhibit wrinkling when heated to a melt sealing temperature of the melt-flowable composition and subsequently cooled, said sheet material being placed on the surface of the step joint such that said melt-flowable composition contacts said surface of the step joint;
- (b) heating the sheet material to a melt sealing temperature sufficient to cause said melt-flowable composition to (1) melt, flow and level out over surface imperfections or fill gaps in the step joint, as well as (2) adhere and form a bond to the step joint;
- and
- (c) allowing the sheet material and the step joint to cool while substantially retaining said surface topography of said film,
- wherein the melt-flowable layer is thick enough to provide sufficient material to flow and seal the step joint, the sheet material remains adhered to the step joint, and topographical or protective features are imparted to the step joint by the sheet material.
2 more elements