Hot melt binder for asphalt product with reduced production temperature and applications of said binder
AssigneeColas
InventorJean-Pierre Dean
Life of this patent
Estimating the term…
Abstract
The binder is produced based on natural bitumen, or bitumen from the oil industry, and comprises a first additive which is constituted by a hydrocarbon wax whose melting point is greater than 85° C. This binder further comprises a fatty acid ester wax which is of synthetic, vegetable or fossil vegetable origin and which has a melting point of less than 85° C. Use in the production of sealing coatings for buildings or civil engineering works, coatings for traffic routes or urban amenities.
Claims26
Asphalt product which can be hot-poured and which hardens by means of simple cooling, of the type comprising mineral fillers such as fines, sand and optionally gravel;
- and a thermofusible binder, this binder being based on natural bitumen or bitumen from the oil industry, of the type comprising, in addition to this base product, a first additive which is constituted by a hydrocarbon wax which is substantially insoluble in the base bitumen of the binder at ambient temperatures and whose melting point, measured in accordance with the standards ASTM D3945 and D3418, is between 110° C. and 140° C., and which reduces the production temperature of the asphalt product relative to that of the base product, characterised in that it further comprises a second additive which is constituted by a fatty acid ester wax selected from montanic acid esters or lignoceric acid esters, this wax having a melting point, measured in accordance with the above standards, of less than 85° C.,
- wherein the binder contains from 4 to 15% by mass of the total formed by the first and second additives relative to the total mass of the binder, and
- wherein the binder contains from 1 to 10% by mass of the second additive relative to the total mass of the binder.
Method for preparing an asphalt product which can be hot-poured and which hardens by means of simple cooling, comprising the following steps:
- (a) a thermofusible binder is mixed with fillers, in particular mineral fillers, such as fines, sand and optionally gravel, this binder is based on natural bitumen or bitumen from the oil industry, of the type comprising, in addition to this base product, a first additive which is constituted by a hydrocarbon wax which is substantially insoluble in the base bitumen of the binder at ambient temperatures and whose melting point, measured in accordance with the standards ASTM D3945 and D3418, is between 110° C. and 140° C., and which reduces the production temperature of the asphalt product relative to that of the base product, characterised in that it further comprises a second additive which is constituted by a fatty acid ester wax selected from montanic acid esters or lignoceric acid esters, this wax having a melting point, measured in accordance with the above standards, of less than 85° C., the binder containing from 4 to 15% by mass of the total formed by the first and second additives relative to the total mass of the binder, and from 1 to 10% by mass of the second additive relative to the total mass of the binder,
- (b) the mixture produced at step (a) is poured, and
- (c) the poured mixture is allowed to cool,
- the steps (a) and (b) being carried out at a temperature of between 150 and 170° C.
Bituminous concrete, of the type comprising mineral fillers such as fines, sand and optionally gravel;
- and a thermofusible binder, this binder being based on natural bitumen or bitumen from the oil industry, of the type comprising, in addition to this base product, a first additive which is constituted by a hydrocarbon wax which is substantially insoluble in the base bitumen of the binder at ambient temperatures and whose melting point, measured in accordance with the standards ASTM D3945 and D3418, is between 110° C. and 140° C., and which reduces the production temperature of the asphalt product relative to that of the base product, characterised in that it further comprises a second additive which is constituted by a fatty acid ester wax selected from montanic acid esters or lignoceric esters, this wax having a melting point, measured in accordance with the above standards, of less than 85° C.,
- wherein the binder contains from 4 to 15% by mass of the total formed by the first and second additives relative to the total mass of the binder, and
- wherein the binder contains from 1 to 10% by mass of the second additive relative to the total mass of the binder,
- characterised in that it contains recovered asphalt which is recycled during production.