Porous landscape pebble and method of manufacturing the same
AssigneesOhonokaihatsu Co., Ltd., Ehimeken
InventorsTeruo Ohono, Masahiko Kan
Life of this patent
Estimating the term…
Abstract
Fly ash containing unburned carbon of at least 10 wt % is pelletized using water as a binder without substantial addition of an inorganic binder, into unsintered particles each having an average diameter of 2 mm to 30 mm. The unsintered particles pelletized are sintered at a temperature which allows the landscape pebble to have a compression strength of at least 50 N and a water absorption rate of at least 40 wt %.
Claims9
A method for manufacturing a porous pebble capable of holding water therein to cool the air, the method comprising:
- a pelletizing process including pelletizing fly ash containing unburned carbon of at least 10 wt % using water as a binder without adding an inorganic binder and of forming the pelletized fly ash into unsintered particles having an average diameter of 2 mm to 30 mm;
- and
- a firing process including sintering the unsintered particles obtained in the pelletizing process at a temperature in a range of 1050° to 1200° so as to obtain a pebble having a compression strength of at least 50 N and a water absorption rate of at least 40 wt %.
A method for manufacturing a porous pebble capable of holding water therein to cool the air, method comprising:
- a pelletizing process including adding a binder to fly ash containing unburned carbon and pelletizing the fly ash into core particles;
- a coating process including coating surfaces of the core particles obtained in the pelletizing process with an inorganic powder containing fly ash having a less content of unburned carbon and a greater content of iron oxide than the fly ash constituting the core particles or an inorganic powder including a fine powder of a rock to thus form a surface layer on the core particles and obtaining unsintered particles having an average diameter of a range 2 mm to 30 mm;
- and
- a firing process including firing the unsintered particles obtained in the coating process to sinter the core particles and their surface layers, making both the core particles and their surface layers porous, and sintering the surface layers at a temperature in a range of 1000° to 1200° so as to provide a strength that is stronger than the core particles while making the core particles porous so as to obtain a pebble having a compression strength of at least 50 N and a water absorption rate of at least 40 wt %